1. Introduction
The deterioration of water quality by organic pollutants has become a global issue of concern that requires an effective solution. According to the European Environmental Agency Report, only around 40% of surface waters (rivers, lakes, and transitional and coastal waters) are in a good ecological status, and 38% are in a good chemical status [1]. Another report, on the quality of 100 rivers from 27 European countries concluded that only about 10% of the river water samples analyzed could be classified as “very clean” in terms of chemical pollution [2]. Pollutants present in water are classified as organic and inorganic and can reach surface waters and groundwaters mainly through industrial effluents, agricultural runoff, sewage plants and other human activities. In general, organic pollutants including aromatic compounds, dyes, pesticides, and antibiotics are toxic and/or resistant to microbial degradation. Once these organic pollutants enter the water bodies, water is no longer safe for drinking purpose and sometimes the complete removal of these pollutants from the water is a very difficult process.
Dyes are released by various industries, such as food, cosmetics and especially textiles [3,4]. According to incomplete statistics, over 35,000 metric tons of dyes are released into the environment [5]. Emerging contaminants, as pharmaceutical and personal care products, pesticides, food additives, surfactants, etc., are present in different water resources in the range of ng L−1–µg L−1 [6]. These compounds are generally non-biodegradable or poorly biodegradable, thus becoming stable and persistent compounds when released into surface and groundwaters [7]. On the other hand, aromatic compounds, as phenols, anilines and polycyclic aromatic compounds, are also environmentally relevant contaminants and can be widely found in the effluents from dyestuffs, pharmaceuticals, petrochemicals, and other industries [8]. In recent years, there has been growing concern about the presence of these compounds in the aquatic environment due to their wide distribution and potential adverse health effects even at low concentration [8,9].
Various water treatment processes have been developed to reduce organic compounds’ levels in waters, such as photocatalysis, ozonolysis, electrolysis, membrane process and adsorption. Among these methods, adsorption is one of the most promising techniques in water remediation due to its low cost, easy operation, the possibility of regeneration and feasibility of application in field conditions [3,6,10,11]. The overall adsorption process consists of the following key steps: (a) pollutant adsorption (b) recovery of the adsorbent for further reuse (c) adsorbent regeneration, and (d) management of both the regeneration solution and the saturated adsorbent. Adsorbent regeneration is a crucial economic factor for industrial applications [5]. Part of the cost that affects the application of the adsorption process lies in the possibility of reusing the adsorbent material several times. Therefore, the adsorbent material must have a good affinity to remove contaminants, be stable (i.e., not lose some of its components by leaching or bleeding) and must be regenerated and used in various adsorption/desorption cycles. To guarantee the reuse of the adsorbent, the separation process of the adsorbents from the aqueous medium is a key step to achieve a good performance and cost-effective treatment. Filtration or centrifugation techniques are often used for the separation process, but both techniques are not cost-effective and are difficult to handle when large volumes of water are used [11]. Moreover, adsorbents may lead to blockage of the filters or loss of adsorbent. To overcome these problems, the use of magnetic nanoadsorbents has been proposed [12,13]. Magnetic separation is an environmentally friendly alternative for the separation and recovery of nanomaterials, since it minimizes the use of solvents and auxiliaries, reduces the operation time, and is a cost-effective method compared to conventional separation processes as filtration or centrifugation [14]. For the reasons outlined above, magnetic adsorbents have emerged as a new generation of materials for decontamination processes [15]. In particular, the most commonly employed magnetic carriers for environmental applications are magnetite (Fe3O4) and maghemite (γ-Fe2O3) nanoparticles, because they are easy to synthesize, environmentally friendly, and have high saturation magnetization. The magnetic properties of iron oxide nanoparticles, in particular of those commonly used in environmental applications, are well documented and reviewed elsewhere and are beyond the scope of this review [16,17]. Bare magnetic iron oxide nanoparticles undergo oxidation/dissolution, especially in acid solutions [15,18], and co-aggregation because of their high surface energy [10,18], and even in environmental conditions their chemical stability can be affected [19], which limits the large-scale application of magnetic iron oxide nanoparticles. Therefore, a large number of functionalized magnetic nanoparticles and magnetic nanocomposites with new structures and surface properties have been produced to overcome the deficiencies of magnetic nanoparticles, provide more active sites and improve their aqueous stability and versatility. Currently, many different materials have been used in combination with magnetic nanoparticles to manufacture magnetic nanoadsorbents, such as silica, activated carbon, carbon nanotubes, polymers, metal–organic frame works, and clays, showing varying extents of effectiveness in removing the organic pollutants from water. Each type of adsorbent nanomaterial has different surface properties, surface chemical groups, and specific areas and pore size. The selection of the appropriate material represents a critical factor to guarantee efficient removal of the organic pollutant.
This review was designed to provide an overview of the synthesis methods, surface properties and application in organic pollutant removal of different magnetic nanoadsorbents. We will present recent scientific progress on the preparation of magnetic core–shell nanoparticles and nanocomposites paying special emphasis on materials with high adsorption capacities. Although there are many review articles in the literature that cover the application of magnetic nanomaterials in the environmental field [13,14,17,20,21,22,23,24], we believe that more specific data gathering is still needed on the synthesis methods and properties of magnetic nanoadsorbents that have been developed so far, and their efficiencies and limitations in the water treatments. This information will contribute to the field of rational design of nanomaterials for water treatment and will help in designing more efficient water treatment technologies to guarantee adequate water quality.
2. Silica-Based Materials
Silica (chemically SiO2) has a three-dimensional network structure that consists of SiO4 and ends with oxygen through siloxane groups (Si–O–Si) or silanol groups (Si–OH) [25]. Silanol groups offer a rich surface chemistry useful in the adsorption process, since they can complex some molecules and metal cations. This interaction can be improved by modifying the pH, due to their acid-basic behavior. In consequence, bare silica can be used as an efficient adsorbent for pollutants, such as dyes, heavy metals and aromatic compounds [26]. Silica nanoparticles can be porous or non-porous. Mesoporous silica (mSiO2) is a unique class of synthetic porous material, with a pore size between 2 and 50 nm. Because of its porosity and higher surface area, mesoporous silica is often preferred as an adsorbent rather than non-porous silica. The highly adjustable structure, versatile surface chemistry, low production cost and simple synthesis procedure are the primary benefits that encourage their application in adsorption. Moreover, silanol groups allow the introduction of a wide variety of functional groups to the silica surface. Therefore, many surface functionalization methods, post-synthesis or during synthesis, have been developed to improve the adsorption capacity and selectivity of mesoporous silica [26,27,28,29,30,31]. The incorporation of iron and iron oxides, such as magnetite and maghemite, to the silica structure is usually carried out by two approaches. One method consists in covering a core of iron oxide nano- or micro-particles with a shell of non-porous silica or mesoporous silica to produce hierarchical structures known as “core–shell” particles (Figure 1A,B). These structures have the additional advantage of protecting the iron-based core from leaching and oxidation in water [32] and, at the same time, of reducing the tendency of aggregation of the particles. In the other method, magnetic particles are dispersed onto mesoporous silica. Wang and co-workers [33] prepared magnetite by the hydrothermal method and they covered with a non-porous silica shell via the Stöber method. The obtained Fe3O4@SiO2 nanoparticles were tested for the removal of anionic dye Congo Red. As expected, the adsorption results were strongly pH dependent. The silanol groups at low pH values are protonated allowing electrostatic interactions between Fe3O4@SiO2 nanoparticles and Congo Red molecules, which leads to a higher dye removal performance. These core–shell type particles can be further modified in different ways. Recently, Cao’s group [34] used the polymer polyvinylpyrrolidone (PVP) to provide affinity to hydrophobic substances to Fe3O4@SiO2 particles. They prepared magnetic cores by the miniemulsion method, then covered them with non-porous silica shell and finally with PVP. The resulted adsorbent (Fe3O4@SiO2-PVP) was tested for the hydrophobic compound phenanthrene. The adsorption reaches the equilibrium fast (10 min), and the maximum adsorption capacity was high compared to previous PAH adsorption reports [35].
The incorporation of silane groups is one of the most common procedures to provide affinity and versatility to an adsorbent for a specific target pollutant [39]. A silane is a group that consists in a central silicon atom bonded to alcoxy groups (usually methoxy and ethoxy) and at least a different moiety with a specific group, such as amino, thiol, hydroxy, vinyl, aliphatic chains, aromatic chains, etc. In a silanization reaction, the surface hydroxyl groups of the solid (e.g., Si–OH in SiO2 or Fe–OH in Fe3O4) react with the alcoxy groups of the silane and form a covalent bond (Si–O–Si in SiO2 and Fe–O–Si in Fe3O4). The work of Sasaki and Tanaka [40] is an example of a simple silanization procedure. They covered commercial magnetite with phenyltrimethoxysilane (PTMS) and studied the adsorption mechanism with several aromatic compounds. The new functionality incorporated by a silane allows further modifications. For instance, the incorporation of vinyl groups by grafting of 3-(methacryloxypropyl)trimethoxysilane (MPS) to Fe3O4@SiO2 nanoparticles allows a radical polymerization reaction to obtain a polymer covering the nanoparticles [41,42]. Jiaqi and co-workers [43] lately proposed a dendritic-like structure to enlarge the magnetic silica nanoparticles area and thus improve their adsorption performance. For this, 3-chloropropyltriethoxysilane (CPTES) were grafted to Fe3O4@SiO2 NPs; then a substitution reaction with ethylenediamine and finally a chemical reaction with maleic anhydride were performed. The obtained carboxylated ethylenediamine functionalizated nanoparticles (Fe3O4@SiO2-EDA-COOH) show remarkable magnetic saturation and high sorption capacity of cationic dye methylene blue and can be reused five cycles. However, the reported maximum sorption capacity of 43.15 mg g−1 corresponds to a relatively high pH of 10.
Wang’s group [44] developed a novel MOF-based smart adsorbent named Fe3O4@SiO2@UiO-67 for the simultaneous selective recognition, detection and removal of organophosphorus pesticide glyphosate for the first time. The prepared adsorbent contains Zr–OH groups with high affinity for phosphate groups, endowing it with an outstanding adsorption capacity for glyphosate. Furthermore, the adsorbent was able to be reused four times with no significant adsorption capacity decrease.
Other types of magnetic silica-based materials use nanoscale zero-valent iron (nZVI) instead of iron oxides as a core. nZVI is commonly applied as a catalyst because of its strong reduction capability. However, there are a few reports of their use to provide magnetic properties to silica-based materials. Li et al. [35] synthesized nZVI nanoparticles coated with silica and polydopamine using a two-step process. The obtained adsorbent (Fe@SiO2@PDA) was applied in the removal of anthracene and phenanthrene from aqueous media, achieving maximum adsorption capacities of 0.185 and 0.367 mg g−1, respectively. Interestingly, the adsorption efficiency of Fe@SiO2@PDA barely decreased after 10 cycles.
Recently, a novel particle system, so-called raspberry-like supraparticles, consisting in magnetite/maghemite and amorphous silica nanoparticles, was studied in the adsorption of methyl blue dye [38]. For the synthesis of these nanoparticles, the method of spray-drying was used: droplets from nanoparticle dispersions were generated in a hot chamber and the solvent was evaporated, forcing the remaining nanoparticles in the droplets together to form supraparticles. The supraparticle system consisted of nanoparticles of 10 nm diameter (Figure 1B) and showed a maximum adsorption capacity of 93 mg g−1. Though this adsorption capacity is comparable or lower than previous reports, the adsorption kinetics results to be outstandingly fast, reaching equilibrium within 60 s. Further, the system can be regenerated either thermally or by acid treatment and can be reused consecutively with a slight loss in adsorption capacity.
Currently, it is of interest to have alternative silica sources rather than synthetic reactants, e.g., from industrial waste, to prepare silica-based materials and adsorbents. This approach could contribute to minimize waste and to apply more economic methods. For instance, silica were obtained from rice husk by calcination and acid leaching and with microwave assistance [45,46]. Additionally, solid waste coal gasification fine slag as the silica source successfully produced mesoporous glass microspheres with a specific surface area of 364 m2 g−1 and an adsorption capacity of 140.57 mg g−1 in methylene blue removal [47]. Recently, silica obtained from rice husk has been used to incorporate an amorphous silica shell onto magnetite obtaining core–shell nanoparticles [45]. These particles were then amino-functionalized with (3-aminopropyl)trimethoxysilane (APTMS) and tested in the adsorption of methylene red dye.
The preparation of core–shell magnetic mesoporous silica is generally a multi-step procedure: synthesis of magnetic nanoparticles, coating with mesoporous silica, removal of template, and functionalization of the mesoporous silica shell. Among the many synthesis procedures for mesoporous silica [28], the hydrothermal method, based on the sol–gel Stöber method, is the most frequently reported for adsorbent preparation. This process consists in the polymerization of a silica precursor (e.g., TEOS) directed by micelles of a templating agent that lead to a mesoporous silica covering formerly prepared magnetic cores in a perpendicularly aligned pore arrange. Then, the templating agent remaining inside the pores is usually removed by calcination [37] or reflux in ethanol/acid water mix [48]. The pore size, particle size and morphology of mesoporous silica can be adjusted by selecting different template agents, by controlling pH and by using additives [29]. For instance, the synthesis of MCM-41 typically involves the cationic surfactant cetyltrimethylammonium bromide (CTAB); meanwhile, the neutral co-polymer with larger molecular weight Pluronic P-123 is used in preparation of SBA-15 [30]. Adding a co-solvent, like trimethylbenzene (TMB), to expand the micelle formed by the templating agent is another way to obtain wider pores [49]. Finally, the functionalization of mesoporous silica can be done post-synthesis or even during synthesis.
Zhang and co-workers [37] prepared these kinds of magnetic silica-based particles functionalized with cyclodextrins and they tested them as an adsorbent of the antibiotic doxycycline (DOX). Cyclodextrins (CDs) are a class of macrocyclic molecules with a hydrophilic exterior and a lipophilic interior cavity, and they can form inclusion complexes with organic molecules, which can be trapped in the hydrophobic cavity through multiple interactions, including inclusion interactions, hydrophobic interactions, electrostatic attractions, and π–π interactions. First, magnetite was prepared via the solvothermal method and later these particles were covered with a non-porous silica layer through a modified Stöber method. The as-prepared Fe3O4@SiO2 microspheres were put in a water solution of CTAB and triethanolamine; then, TEOS was added and a mesoporous silica layer covering the microspheres was formed. After calcination, Fe3O4@SiO2@mSiO2 microspheres were obtained (Figure 1C). To introduce covalently bound cyclodextrins, the Fe3O4@SiO2@mSiO2 microspheres were added to a basic water/ethanol solution containing APTMS and monochlorotriazinyl β-cyclodextrin (MCT-β-CD). The obtained Fe3O4@SiO2@mSiO2-CD microspheres showed a maximum DOX adsorption capacity of 78 mg g−1 at initial pH of 3.8. The pH of the DOX solution significantly affected the adsorption process, which is spontaneous at 298 K. The contact time required for antibiotic adsorption using this adsorbent is short compared to activated carbon.
In order to develop a simple synthesis procedure amenable to scale-up, some authors propose the functionalization of mesoporous silica during synthesis. One method consists in the co-condensation reaction adding a silane along with the primary silica precursor in the presence of a surfactant, thus obtaining structures known as periodic mesoporous organosilicas [50]. Cai’s group reported the first one-pot synthesis of functionalized magnetic mesoporous silica composites for the adsorption removal of organic dyes from water [51]. The adsorption of methyl blue on the obtained adsorbent, here termed as Fe3O4@mSiO2–C18, has a negligible influence of solution pH in the range of 4.5–9.5 with an optimal at pH 7.5 and a maximum adsorption capacity of 363 mg g−1 according to the Langmuir model. Furthermore, the adsorption equilibrium was achieved within a relatively short period of time (20 min), because of the high surface area and short adsorption path of mesoporous solid. Another approach is the work of Keller’s group [52] in which the surfactant 3-(trimethoxysilyl)propyl-octadecyldimethyl-ammonium chloride (TPODAC) was used as a templating agent to prepare permanently confined micelle array core–shell nanoparticles. Maghemite cores were surrounded by TPODAC and TMB as a micelle-swelling agent, and then TEOS was added to covalently bind the surfactant onto the magnetic cores. Three different TMB:TPODAC weight ratio were tested. The authors studied the adsorption performance of the as-prepared nanoparticles (γ-Fe2O3@mSiO2-TPODAC) on methyl orange, sulfamethoxazole, gemfibrozil, acenaphthene and phenanthrene. It was found that larger amounts of TMB (TMB:TPODAC 60%) results in a noteworthily higher sorption kinetic rate as well as slightly higher sorption capacity. In addition, the core–shell nanoparticles showed good adsorption capacity after five regeneration cycles. The nanoparticles show relatively low surface area and magnetic saturation; however, they proved to be a versatile adsorbent for dyes, ECs and PAHs.
Composites consisting of magnetic nanoparticles dispersed in a mesoporous silica matrix were also developed and applied as adsorbents. Ghanei [53] prepared iron oxide nanoparticles embedded in SBA-15 mesoporous silica functionalized with 3-methacryloxypropyltrimethoxysilane followed by a polymerization with acrylic acid monomer. The obtained adsorbent M-SBA-15/CPAA proved to have a noteworthy adsorption capacity towards Acid Blue 25 dye. However, the adsorption process proved to be strongly pH-dependent and the maximum corresponds to highly acid conditions (pH 2). Other composites functionalized via polymerization onto silica surface were used for removal of the dyes [54].
Hollow mesoporous silica spheres (Figure 1D), in contrast with conventional mesoporous silicas such as MCM-41 and SBA-15, have some additional features including low density, high adsorption capacity, high storage capacity and permeability, turning them into promising materials for applications in drug delivery, catalysis and adsorption [36]. Thus, the preparation of nanocomposites with magnetic cores inside the cavities of hollow mesoporous silica spheres, namely rattle-type or yolk-shell magnetic mesoporous silica nanocomposites, is of great interest for a variety of environmental applications. The study of Jin and co-workers [55] is the first report about the adsorption capacity of rattle-type nanoparticles. The synthesis consists in preparation of magnetic particles, covering with silica and a sacrificial template (resorcinol-formaldehyde resin polymer), a further layer of mesoporous silica and calcination to remove the organic matter. The prepared spheres, here named γ-Fe2O3@SiO2@h-mSiO2, present a similar fast removal rate of methyl blue to mesoporous MCM-41. The adsorption capacity increase with the pH, with a value of 41 mg g−1 at pH 7.2.
Table 1 summarizes the adsorption capacities and some physicochemical properties of the silica-based nanocomposites described in this section.
3. Clay-Based Composites
Clays are naturally occurring adsorbents, although their hydrophilic character and natural negative charge limits the adsorption capacity of many hydrophobic organic pollutants and anionic compounds [4,58,59]. Despite this, their swelling capacity and ability to interleave and/or graft different substances makes them as a very attractive option to develop different composites. Several techniques, such as the incorporation of organic cations, polymers and metals using pillaring, have been used to modify the surface and structural properties of clays [60,61,62,63]. Adsorption studies using modified clay minerals as adsorbents have shown remarkable results [60,64,65]; however the small particle size and low density of these materials makes it difficult to separate them from the aqueous solution [66]. Therefore, conferring magnetic properties to clay minerals could open a wide range of possibilities for water treatment. The preparation of magnetic clay mineral composites has been the subject of various studies [3,4,6,10,11,67,68]. The interlayer space, channels, siloxane surfaces and edges of the clay minerals provide hosting sites to stabilize magnetic NPs, thus leading to the formation of magnetic nanoparticles/clay mineral nanocomposites [18]. Typical synthesis routes to prepare magnetic clay minerals nanocomposites are pillaring, coprecipitation and intercalation (Figure 2). Pillaring represents a simple synthesis route where two strategies are possible; the combination of magnetic NP and pillared clay mineral, where the pores of the pillared clay minerals host the magnetic NPs (route A1, Figure 2), or the use of magnetic NPs as pillars to expand the interlayer space of clay mineral in order to create magnetic pillared clay mineral nanocomposite (route A2, Figure 2). Co-precipitation is the other simple and widely used route of synthesis, based on the in-situ formation of the magnetic NPs in an aqueous dispersion of clay mineral (route B, Figure 2). The intercalation method is usually used in two ways; on the one hand, using surfactant-modified magnetic NP, which is stabilized into clay mineral (route C1, Figure 2), and on the other hand, the inclusion of magnetic NP into surfactant intercalated clay mineral, where the surfactants change the surface and expand the interlayer space of the clay minerals to match and facilitate the entrance of the magnetic NPs (route C2, Figure 2).
Expansible and non-expansible clay minerals have been used to prepare magnetic nanocomposites. Magdy et al. [10] prepared magnetic nanocomposites of kaolin and magnetite (Fe3O4/kaolin) by the co-precipitation method in one step, and tested the prepared nanocomposites as adsorbents in the removal of the anionic Direct Red 23 dye. They achieved a complete removal of dye under the following set of operating conditions: initial dye concentration = 20 mg L−1, adsorbent mass = 0.75 g, T = 25 °C and pH 7. Additionally, the adsorption followed the Langmuir isotherm with a maximum adsorbent capacity of 22.88 mg g−1. On the other hand, Chang et al. [4] prepared magnetic nanocomposites from montmorillonite (Mt) and magnetite (Fe3O4/Mt) by a co-precipitation method. This study revealed that Fe3O4 nanoparticles are present on the surface of Mt. The magnetic nanocomposite showed a good adsorption efficacy (99.47%) in methylene blue removal.
Another possibility of very interesting modification results from the preparation of magnetic clay mineral nanocomposites with the incorporation of one or more extra components to improve some of the mentioned properties or incorporate new ones. Mu et al. [69] developed several magnetic nanocomposites combining in-situ intercalation, polymerization and coprecipitation techniques. They polymerized aniline molecule, during the synthesis of Fe3O4 in a suspension of Mt, obtaining polyaniline (PANI) and Fe3O4 supported on the surface of Mt (Mt/PANI/Fe3O4). They tested these materials in the adsorption of three dyes, methylene blue, brilliant green and congo red. One of the developed nanocomposites removes 99.6%, 96.2% and 98.1% of methylene blue, brilliant green and congo red, respectively, from 100 ppm dye solutions, with nanocomposite dosages of 1 g L−1, at 25 °C. They also studied the reuse of Mt/PANI/Fe3O4 using BM, and after five cycles the adsorption capacity did not decrease (in all cases it was close to 100%).
Arya and Philip [6] incorporated powdered-activated carbon, chitosan and sodium tripolyphosphate as a binding agent to magnetite nanoparticles supported in bentonite, with the aim of developing a new adsorbent compound capable of removing anionic, cationic, hydrophilic or hydrophobic contaminants. They studied the efficiency of this adsorbent to remove atenolol, ciprofloxacin and gemfibrozil from aqueous systems. The authors found a high removal of atenolol and ciprofloxacin (85% and 95% respectively, with an adsorbent dosage of 1.5 g L−1), which can be attributed to the hydrophilic nature and the interchange capacity of clay–chitosan, since both pollutants are predominantly cationic at the working pH. On the other hand, the hydrophobic nature of activated carbon may be the main factor in the adsorption of genfibrozil (90% removal).
Diagboya and Dikio [11] developed magnetic adsorbent composites with feldspar clay (FLC), pericarp of oak fruits (PER) and magnetic nanoparticles. The nanocomposites were prepared by the co-precipitation method in the presence of FLC free of organic matter and sieved PER; then, the product obtained was pyrolyzed at 250 °C for 4 h. Magnetic adsorbents (BMF-0.5 and BMF-1) were used to study the removal of methylene blue. The authors performed three adsorption/desorption cycles of methylene blue; they observed that the adsorption capacity decreases in each cycle. The second cycle was lower than the first by approximately 7% for both nanocomposites and the third cycle decreased by a similar proportion.
On the other hand, Fizir et al. [68] developed magnetic halloysite nanotubes (MHNTs) by the method of co-precipitation followed by polymer grafting onto the nanocomposites, to adsorb norfloxacin. Combining the advantages of the high adsorption capacity and the magnetic properties of this biocompatible clay nanotube and the advantage of the polymer shell in improving the controlled and sustained release of the drug, they formulated a novel bioactive agent.
Beé et al. [3] used an extrusion method to obtain a magnetic adsorbent that was prepared by trapping maghemite nanoparticles (γ-Fe2O3) and montmorillonite (MMT) in cross-linked chitosan (CS) beads, in order to obtain an efficient adsorbent for cationic and anionic contaminants. They prepared pearls with different clay contents and performed adsorption experiments with methylene blue. They observed that the adsorption capacity of methylene blue increased as the amount of clay increased and the increase occurred over the entire pH range studied (3-12). The maximum uptake of methylene blue (82 mg g−1 at pH 9.9) was obtained with the material that had the highest proportion of clay; this indicates that the adsorption properties of the clay were not affected by encapsulation in the beads. Table 2 summarizes the adsorption capacities of the magnetic-clay-based nanocomposites described in this section.
4. Carbon-Based Materials
Different carbon-based materials have been utilized for adsorption of pollutants, including activated carbon, graphitized carbon black, porous carbon, graphene oxide (GO) and carbon nanotubes (CNTs), due to the versatility of types of interactions that can accomplish with pollutants, such as electrostatic, hydrophobic and π–π interactions [70]. These materials differ in their structures and physicochemical characteristics, as pore size/shape, pore volume, surface area and surface functionality. For instance, CNTs can be considered as hollow graphitic nanomaterials comprising one (single-walled carbon nanotubes, SWNTs) or multiple (multiwalled carbon nanotubes, MWNTs) layers of graphene sheets, while GO is a derivative of graphene, which has abundant active functional groups such as carboxyl, hydroxyl and epoxy [71].
During the last decade, much effort has been devoted to developing efficient synthetic routes to shape-controlled, highly stable, and well-defined magnetic carbon hybrid nanocomposites. Several methods including the filling process, template-based synthesis, chemical vapor deposition, the hydrothermal/solvothermal method, the pyrolysis procedure, the sol–gel process and the self-assembly method can be used for the synthesis of high-quality magnetic carbon nanocomposites [72].
A list of magnetic carbon-based nanocomposites with their adsorption capacity for organic contaminants and some physicochemical properties has been summarized in Table 3. In some cases, the magnetization of the carbon-based materials enhances the adsorption properties when compared to the pristine carbon material. This is explained considering that magnetic nanoparticles can increase the porosity of carbon materials, which favor the diffusion of contaminants to more available adsorption sites.
Fe3O4 supported on reduced Grapheme Oxide (rGO) nanocomposite for the removal of harmful pesticides, namely simazine, simeton, atrazine, prometryn, and ametryn, was synthetized by Boruah et al. [73] using an eco-friendly in-situ solution chemistry approach, GO was synthesized from graphite powder and reduced to the rGO sheet using ascorbic acid as a reducing agent. Then, Fe3O4 nanoparticles were synthesized adopting the chemical co-precipitation method in the presence of rGO, yielding Fe3O4/rGO nanocomposite. Their study reveals that Fe3O4/rGO nanocomposite exhibits excellent adsorption performance towards the adsorption of the five pesticide molecules, compared to Fe3O4 nanoparticles and rGO sheets. The corresponding adsorption efficiencies for simazine, atrazine prometryn, ametryn, and simeton were found to be 88%, 75%, 91%, 93% and 81%, respectively.
In general, carbon-based nanomaterials have a unique π–π electronic structure that provides excellent properties to be used as adsorbents for the removal of aromatic compounds [74,75]. Yang et al. [76] compared the adsorption capacity of aromatic compounds (1-naphthylamine, 1-naphthol and naphthalene) between reduced graphene oxide/iron oxide composites (GO/Fe3O4) and multi-walled carbon nanotube/iron oxide composites (MWCNTs/Fe3O4). They found that electron–donor–acceptor (EDA) interaction was the primary adsorption mechanism and the higher polarity of adsorbates lead to higher adsorption capacity. In particular, GO/Fe3O4 showed better adsorption capacity than MWCNTs/Fe3O4, probably due to GO/Fe3O4 presenting more available and abundant adsorption sites.
Fan et al. [77] prepared magnetic β-cyclodextrin–chitosan/graphene oxide materials (MCCG) via a chemical route to remove methylene blue from aqueous solution. In this synthesis procedure, the carboxyl group of GO chemically reacts with the amine group of the magnetic β-cyclodextrin–chitosan composite to yield the magnetic carbon-based sorbent. MCCG showed excellent sorbent properties, benefiting from the high surface area of graphene oxide, hydrophobicity of β-cyclodextrin and the abundant amino and hydroxyl functional groups of chitosan. The maximum adsorption capacity of MCCG was 84.3 mg g−1, which was higher than those reported for other adsorbents such as graphene/magnetite composite (43.8 mg g−1), pyrophylite (4.2 mg g−1), carbon nanotubes (46.2 mg g−1), exfoliated graphene oxide (17.3 mg g−1) and β-cyclodextrin–chitosan (50.12 mg g−1) [78,79,80]. Among other magnetic carbonaceous materials with high sorption capacity to remove methylene blue, magnetic graphene sponge, (Fe3O4-GS) synthetized using a simple method, in which Fe3O4 nanoparticles are mixed with GO and subsequently lyophilized to obtain Fe3O4-GS, was reported by Yu et al. [81] This magnetic graphene sponge presents quite high adsorption capacity for MB (526 mg g−1) and facile regeneration.
Alizadeh Fard and Barkdoll [82] prepared magnetic carbon nanotubes (MCN) to remove six micropollutants (Metolachlor, Bisphenol-A, Tonalide, Triclosan, Ketoprofen and Estriol) from water. In this work, to prevent the formation of other species of iron oxide, the synthesis of MCNs was performed separately: first, the magnetic nanoparticles were produced by a simple hydrothermal method. Then, the magnetic nanoparticles were mixed with the HNO3-treated CNTs. MCN presented good adsorption capacity in which Bisphenol-A, Ketoprofen and Tonalide were the most effectively removed micropollutants, with 98%, 96% and 96% removal within 47 min, respectively.
Gong et al. [83] developed magnetic multi-wall carbon nanotube (MMWCNT) nanocomposite using a modified sol–gel process. The negatively charged MMWCNT surface over a wide pH range is one of the main characteristics that allows the removal of cationic pollutants. The adsorption properties of this adsorbent were examined using cationic dyes (methylene blue, neutral red and brilliant cresyl blue). They observed that dye adsorption capacity increased when pH increased from 3 to 7, while beyond 7, the adsorption capacity was not significantly altered. The comparison of the adsorption results with MWCNT and activated carbon indicated that MMWCNT nanocomposite showed the main advantage of the convenience of separation compared to the adsorption treatment in aqueous media. By using another synthesis strategy, Zhao et al. [84] prepared MWCNTs decorated with Fe3O4 nanoparticles modified with polyaniline (MWCNTs/Fe3O4/PANI) and used this material to test the adsorption of methyl orange and Congo red. The MWCNTs/Fe3O4/PANI showed high adsorption capacity toward the tested dyes (446.25 mg g−1 for methyl orange and 417.38 mg g−1 for congo red). The nitrogen containing functional groups of PANI, along with the synergistic effect between MWCNT π-conjugated bonds and PANI π-conjugated bonds, contribute to boosting the effective adsorption sites and thus increase the adsorption capacity toward MO and CR. Another important result obtained from the authors is that the presence of PANI prevented Fe3O4 nanoparticles from dissolving, and hence improved the stability of MWCNTs/Fe3O4/PANI in solution. In order to confer more carboxyl groups to magnetic carbon nanotube nanocomposites, Deng et al. [85] prepared carbon dot-modified magnetic carbon nanotubes (CMNTs) by three consecutive steps including the preparation of MWNTs, the synthesis of carbon dots and the surface modification of MWNTs using carbon dots. This adsorbent has a moderately high adsorption capacity of carbamazepine (65 mg g−1 at pH 7) and can be regenerated and reused up to six times with capacity loss less than 2.2%.
Liu et al. [86] assembled activated carbon and Fe3O4 nanoparticles (Fe3O4/AC) by a facile one-step thermal decomposition process and tested Fe3O4/AC for the adsorption of rhodamine B and methyl orange. Fe3O4/AC showed a high surface area (about 1200 m2 g−1), which was much higher than pure AC (about 750 m2 g−1), and wide pore size distribution. These properties benefit the adsorption and the rapid inter-diffusion of the dye molecules through interconnected channels. The obtained magnetic composite exhibited better adsorption of the dyes than its pure AC counterpart. Another approach to assemble Fe3O4 nanoparticles with activated carbon was reported by Shan et al. [87] through the ball milling method. They obtained two ultrafine magnetic activated carbon (Fe3O4/AC) and biochar (Fe3O4/BC) hybrid materials. The use of biochar drastically increased the surface area of the magnetic composite, while in case of AC the surface area decreased, probably because some pores in AC are blocked by the Fe3O4 nanoparticles produced in the milling process. However, in both cases, the authors obtained a higher adsorption capacity than pristine carbon materials using two pharmaceuticals as model contaminants (i.e., carbamazepine and tetracycline). On the other hand, Yu et al. [88] reported a higher sorption capacity of tetracycline (473 mg g−1) using a magnetic graphene oxide sponge (Fe3O4-GOS) as sorbent. The material was prepared by lyophilizing the dispersion of Fe3O4 nanoparticles and graphene oxide (GO).
In the study performed by Lompe et al. [89] the adsorption capacity for nine micropollutants (Diclofenac, Fluoxetine, Estradiol, Norethindrone, Atrazine, Carbamazepine, Deethylatrazine, Sulfamethoxazole and Caffeine) on fresh and aged magnetic powdered activated carbon (MPAC) was investigated. They demonstrated that MPAC produced via co-precipitation can be customized with respect to its magnetic properties without compromising its adsorption capacity beyond the reduction expected for lower powdered activated carbon (PAC) contents. Maximum adsorption capacities of PAC and MPAC for all pollutants ranged between 1 and 80 mg g−1.
5. Polymer-Based Materials
Polymers can be chemically anchored or physically adsorbed on magnetic nanoparticles to form a core–shell structure, acting as a protective layer and simultaneously providing active sites to adsorb pollutants. The core–shell structured can be synthesized by using the seed polymerization method and surface-modified Fe3O4 particles as the seeds [90]. This method allows the development of novel porous materials with high surface area and porosity to improve their adsorption performances [91].
Fe3O4@polyaniline, a typical Fe3O4-based magnetic core–shell material, was synthesized for the removal of pollutants such as humic acid, separation of organic dye, extraction and analysis of phenolic compounds and analysis of pyrethroids in tea drinks and polycyclic aromatic hydrocarbons [92]. As a magnetic core–shell material, polyaniline shows great promise, because it can effectively decrease the chance of aggregation, enhance the adsorption properties for organic pollutants via π–π and van der Waals interactions, and improve the stability of magnetic core–shell composites. However, the most appropriate composition of core–shell structure demands that the ratio between magnetic core and shell dimensions be optimized, since insufficient core magnetic oxide could determine a limited magnetic response and insufficient polymer component could result in poor adsorption capacity. Furthermore, to increase the maximum adsorption capacity and the versatility of the nanomaterials, several functional groups such as carboxylate, phosphate, sulfate, hydroxyl, amino and amide groups have been explored for the modification of conventional adsorbents. Hou et al. [93] prepared a core–shell nanoadsorbent based on Fe3O4 nanoparticles surface-modified with a copolymer, using 2,4-diaminophenol and formaldehyde for the adsorption of anionic dyes (amaranth, orange II and acid red 18) and obtained good adsorption capacities, fast adsorption processes and high saturation magnetization.
Liu et al. [94] reported the synthesis of magnetic nanospheres functionalized with β-cyclodextrin (β-CD) by the one-pot solvent thermal method using β-CD immobilized Fe3O4 magnetic nanoparticles with tetra-fluoroterephthalonitrile as the monomer. This material showed fast adsorption kinetics for methylene blue, high dispersibility in aqueous phase, a short equilibrium time (5 min), high recovery and good recyclability (keeping the adsorption efficiency above 86% after five uses). The maximum adsorption capacity of methylene blue was 305 mg g−1.
During the last decade, porous organic polymers, including polymers of intrinsic microporosity [95], metal–organic frameworks (MOFs) [96], covalent organic frameworks (COFs) [97], porous aromatic frameworks [98] and hyper-cross-linked polymers (HCPs) [99] have attracted extensive interest because they have the advantages of low density, excellent chemical and physical stabilities, high surface area, easy control of pore size and functional modification [100]. MOFs are coordination polymers with intriguing structural motifs that can be self-assembled from organic ligands and metal ions or clusters of metal ions. In the last years, MOFs have been developing rapidly and have actually attracted extensive attention in the field of porous materials due to their high surface areas, with a range from 1000 to 10,000 m2 g−1, and a permanent porosity that is superior to those of porous materials such as activated carbon and zeolites [101]. While the use of MOFs as sorbents in gas phase is well-known, some MOFs show limitations in liquid phase adsorption due to their relatively low stability in water and their hydrophilic nature. However, in recent years, the development of water-stable MOFs has increased considerably [102]. Numerous different synthetic approaches, including slow diffusion, hydrothermal, electrochemical, mechanochemical, microwave-assisted heating and ultrasound can be applied to produce MOFs relying on the resulting structures and features [103]. Several magnetic adsorbents with MOF structure have been synthesized. Yang et al. [104] synthesized a new type of Fe3O4@MOF magnetic porous composite material with a core–shell structure of Fe3O4 nanoparticles coated with petal-like ZIF-67 crystals (Zeolitic imidazolate framework-67), in which Co2+ firstly combines with SO32− provided by poly-styrenesulfonate sodium salt to form nucleation. This adsorbent showed high adsorption capacity for methyl orange (anionic dye) owing to the nature of Lewis base coordinated Co(II) and its high porosity. The equilibrium adsorption capacity was as high as 738 mg g−1, which was significantly higher than other adsorbents like coconut shell activated carbon (368 mg g−1) and clay (300 mg g−1) [91]. Hamedi et al. [105] produced a magnetic MOF for the elimination of malachite green and methyl red from wastewaters. Metal–organic framework (MIL-101(Fe)) was prepared from FeCl3 and terphthalic acid. Moreover, they used an extremely tinny film of 3, 4-dihydroxy-Lphenylalanine (PDopa) as an eco-friendly and effective binder between MIL-101(Fe) and Fe3O4 nanoparticles, in order to prevent detachment of the MOF from the magnetic material. In this regard, the authors were able to obtain the perfect capacities of adsorption (833 and 1250 mg g−1 for malachite green and methyl red, respectively). Moreover, the MIL-101(Fe)@PDopa@Fe3O4 adsorbent can be used almost four times to remove dyes. Wu et al. [106] prepared magnetic copper-based MOF (Fe3O4/HKUST-1) as an effective and recyclable adsorbent for the removal of ciprofloxacin and norfloxacin (two fluoroquinolone antibiotics) from aqueous solutions. The maximum adsorption capacities of the magnetic composites toward ciprofloxacin and norfloxacin reached 538 mg g−1 and 513 mg g−1, respectively, noticeably higher than those values of most of the reported adsorbents for these two compounds.
Covalent organic frameworks (COFs), an emerging class of ordered crystalline porous polymers, are constructed from light elements and linked to organic monomers by strong covalent bonds that have an ordered π-structure with pore uniformity. In general, COFs are derived from MOF. They show comparable surface areas, ordered channel structures, well defined pore apertures, low densities, and thermal and chemical stability [91]. COFs with various functionalities and high crystallinity have been synthesized and several materials have been reported in the environmental field. Functionalized crystalline polyimide, polycationic and polyanionic COFs have been used for the removal of contaminants with varying physical and chemical properties. It is noteworthy that the size-sieving effect played a major role in the application of COFs for the removal of pollutants. Based on the literature, COFs’ high surface areas (e.g., 3500 m2 g−1) give COFs more potential as adsorbents than zeolites or activated carbon [107]. Strategies to obtain water-stable materials with highly ordered structures and large surface areas are reviewed. By means of post-synthetic modification approaches, pore surfaces can be tuned to target specific contaminants based on size-dependent separation and charge-selective separation. Immobilization of COFs on solid substrates is a strategy to improve stability and dispersibility, while taking advantage of the properties of all materials present in the composite [108]. Yi et al. [109] prepared core–shell-structured magnetic COF nanocomposites (Fe3O4@COFs) for the adsorption of triclosan and triclocarban in aqueous solutions. Fe3O4@COFs was fabricated on the Fe3O4 nanoparticles using an in-situ growth strategy at room temperature via a condensation reaction of 1,3,5-tris(4-aminophenyl) benzene and terephthaldicarbox-aldehyde in the presence of dimethyl sulfoxide. The adsorption behaviors showed high adsorption capacity and fast adsorption of triclosan and triclocarban. Different magnetic COF composites were also reported for the extraction of bisphenols [110] and polycyclic aromatic hydrocarbons (PAHs) [111] from water.
Hyper-cross-linked polymers (HCPs) can be synthesized by using external crosslinker. The porosity can be improved by using various kinds of reactive monomers or different amounts of crosslinking. For instance, Hu et al. (2019) [100] have synthesized a magnetically hyper-cross-linked polymer using benzylamine and benzene as the reactive monomers, which combined the advantage of the amino-modified HCP (HCP-NH2) and the magnetic Fe3O4 nanoparticles to adsorb organic pollutants such as tetracycline, ethyl orange, methylene blue, bisphenol A and 2,4-dichlorophenol in aqueous solution. The magnetic HCP presented high BET specific surface area (532.62 m2 g−1), well-developed mesoporous (0.3786 cm3 g−1) and good magnetic properties. The adsorption experiments indicated that the magnetic HCP-NH2 showed highly efficient adsorption properties for organic contaminants. In particular, the maximum adsorption capacity of the magnetic HCP-NH2 for tetracycline was 694 mg g−1 at 298 K, which was much higher than that of HCP-NH2 (389 mg g−1). Based on the adsorption performance, the authors propose that tetracycline removal was mainly driven by coordination interaction, cation exchange and hydrogen bonding interactions that involve polymer functional groups and magnetite surface groups.
Recently, various biomaterials based on natural polymers have been developed for improving adsorption capacities, increasing environmental compatibility and operating efficiently. Alginate-based composites have been extensively studied for applications in environmental sectors due to their biocompatible, nontoxic, and cost-effective properties [112]. Various alginate-based composites that enhanced adsorption performance have been reported for the removal of various pollutants including dyes, heavy metals, and antibiotics in water and wastewater. Environmental applications of alginate depend partly on the fact that the rich surface functional groups (e.g., carboxyl and hydroxyl) could capture metallic or cationic ions via ion exchange between the crosslinking cations and target pollutants. Alginate beads may serve as a stable matrix for other types of absorbents that are too fine in particle size and too difficult to separate from aqueous solution. Magnetic adsorbents can be developed by encapsulating magnetic functionalized nanoparticles in alginate beads along with different covalently cross-linked agents, such as molecules of different sizes and structures, including adipic dihydrazide, lysine, and poly-(ethylene glycol)-diamines [113,114]. Talbot et al. [115] reported the synthesis of alginate/maghemite nanoparticles for the adsorption of methylene blue. A co-precipitation method in alkaline medium followed by oxidation of magnetite into maghemite led to a stable colloidal dispersion, which was added to sodium alginate solution in order to obtain the magnetic nanocomposite. The nanocomposites showed high adsorption capacity in a wide pH range and a reuse performance higher than 98% even after ten adsorption/desorption cycles. On the other hand, Mohammadi et al. [116] fabricated superparamagnetic sodium alginate-coated Fe3O4 nanoparticles by a co-precipitation method, obtaining good removal efficiency of malachite green (48 mg g−1).
Chitosan is another biopolymer that is widely used in environmental applications, owing to its low-cost source and environment-friendly nature. It has abundant reactive amino and hydroxyl groups, which can serve as binding sites turning it a potential adsorbent for organic pollutant removal [117,118]. Solubility of chitosan in an acidic medium limits its wide application in water treatment; thus, various cross-linking agents such as glutaraldehyde [119], sodium tripolyphosphate [92], and epichlorohydrin [120] offer an important pathway to improve its chemical stability and extend its potential applications. Zheng et al. [121] prepared poly([2-(methacryloxy)ethyl] trimethylammonium chloride)-grafted magnetic chitosan microparticles via free radical polymerization to obtain novel superior adsorbents with a huge electrostatic “force field” for capturing food dyes. The nanocomposite morphology was nearly spherical with approximately 125 μm average diameters, with a specific surface area of 150 m2 g−1 and average pore diameters of 33.8 Å. Compared to unmodified adsorbents, the adsorption capacities toward Food Yellow 3 and Acid Yellow 23 were considerably enhanced after modification, indicating that the dyes were captured by electrostatic interaction and ion exchange. On the other hand, polymer-grafted magnetic microspheres (GMMs) were prepared by graft polymerization of 2-acrylamido-2-methylpropane sulfonic acid and acrylic acid onto the surface of chitosan/magnetite composite microspheres and were used as an adsorbent to remove methylene blue from aqueous solutions [122]. The authors reported a maximum adsorption capacity for methylene blue of 926 mg g−1, which is notably higher than the reported values for other adsorbents. Table 4 shows the adsorption capacities of the polymer-based magnetic nanomaterials with higher organic pollutant uptake.
6. Waste-Based Materials
Within the framework of the circular economy, several efforts have been made to add value to wastes, converting them into renewable raw material for the production of fine, bioplastic and auxiliary chemicals for technological and environmental applications. In particular, the modification of different industrial and household wastes into adsorbent materials has been the subject of much research, since it represents an economically sustainable method of waste valorization [128,129,130]. Among them, the most common are agricultural residues, for example the skin of different fruits and vegetables, remnants of branches and leaves, remnants of rice, corn, olive and many others. The reuse of waste from the paper industry, the metallurgical industry, cement and sludge from water treatment plants has also been studied [131].
For the synthesis of waste-derived magnetic materials, most studies use magnetite nanoparticles as the magnetic agent to modify the starting adsorbent sourced from wastes. Safarik and co-workers published two short studies in which they synthetized magnetic adsorbents by putting a stable suspension of magnetite in contact with powdered peanut husk and pine sawdust, respectively [132,133]. They tested these materials against a broad spectrum of organic dyes, obtaining, in particular, maximum adsorption capacities for crystal violet of 80.9 and 51.2 mg g−1. Zuorro et al. [134] achieved remarkable adsorption performance for a waste-derived magnetic material obtained from a similar procedure, in which a suspension of coffee silverskin wastes was mixed with magnetite ferrofluid for 1 h at room temperature. This magnetic adsorbent was tested for methylene blue adsorption, achieved an adsorption capacity of 556 mg g−1 within 2 h at pH 6, and showed good reusability potential, with only a 14% decrease in adsorption after eight regeneration cycles with HCl. Minh et al. [135] also obtained a magnetic adsorbent from ground coffee wastes with an adsorption capacity toward methylene blue of 128 mg g−1. On the other hand, Stan et al. [136] studied four different magnetite–starch materials prepared through an environmentally friendly synthetic route which consist of a co-precipitation method using water as the solvent and sodium bicarbonate as the precipitating agent. One of the four materials was made using bare magnetite and the other three used magnetite synthetized with fruit waste vegetable extract as surfactant. Removal efficiencies of optilan blue dye were between 72% and 89% for these materials. The authors also found that the use of fruit extract in the magnetite synthesis did not improve adsorption performance.
Another method to prepare waste-derived magnetic materials consists in the synthesis of magnetite nanoparticles in an aqueous system where the adsorbent is previously dissolved. Aydin and co-workers used a high-alkaline waste which is produced by the Bayer process in aluminum production called “red mud” and used it along with Fe(II) and Fe(III) salts to synthesize a magnetic-red mud material for adsorption of organophosphorus pesticides and antibiotics [137,138]. With an isoelectric point near eight, this material showed relatively low adsorption capacity towards pesticides, in the order of µg g−1, and good performance against antibiotics with a maximum adsorption capacity of 200 mg g−1 for ciprofloxacin. Madrakian et al. [139] used the solid fraction of tea leaves previously washed and boiled, and tested the obtained magnetic adsorbent performance for seven common cationic and anionic organic dyes. The maximum adsorption capacities for the seven dyes were between 82 and 128 mg g−1. Similar results were obtained by Madrakian et al. [140] using Platanusorientalis tree leaves as a raw material for the production of waste-derived magnetic materials. The adsorption capacities of five dyes were between 89 and 133 mg g−1. The authors claim there is no significant loss in adsorption capacity after ten adsorption–desorption cycles for this material. Jodeh et al. [124] prepared magnetic cellulose-based materials from olive industry solid waste and tested the adsorption performance of these materials with methylene blue. In this study, the cellulose was extracted in a powder form by a multistep pulping and bleaching process. The extracted powder cellulose was converted to nanocrystalline cellulose (NCs) by acid hydrolysis and finally dispersed in an aqueous solution of Fe(II) and Fe(III) to obtain magnetic cellulose nanocrystalline through a co-precipitation method. The magnetic material showed good methylene blue adsorption capacity, ranging from 148 to 196 mg g−1. Sun et al. [141] synthetized a magnetic material from wastes of Vallisneria natans, a widespread fast-growing aquatic plant, using a chemical co-precipitation method. This material achieved an outstanding methylene blue adsorption capacity (474 mg g−1), almost constant in a wide range of pH values (from 5 to 9).
Yu et al. [142] prepared magnetic modified biomass from beer yeast and tested the adsorption potential by using methylene blue and basic violet as model dyes. The magnetic material was prepared by two steps that included the preparation of pyromellitic dianhydride (PMDA)-modified biomass in N,N-dimethylacetamide solution and the preparation of magnetic PMDA-modified biomass by a co-precipitation method under the assistance of ultrasound irradiation. The modified biomass achieved maximum adsorption capacities of 609 and 521 mg g−1 for methylene blue and basic violet, more than six times higher than the unmodified biomass adsorbent. Increasing pH showed a positive effect on adsorption capacities, showing values above 300 mg g−1 over a pH range between 3 and 9.
Core–shell magnetite nanoparticles, using soluble organic matter extracted from urban public park trimming and home gardening residues as a covering material, were used as sustainable and removable magnetic adsorbent materials [143,144,145]. The soluble organic matter (SBO) was obtained through 230 days of green residues composting followed by alkaline digestion and ultrafiltration of the soluble matter. Magnacca et al. [143] used the obtained Fe3O4-SBO nanoparticles for crystal violet removal from waters, and the results showed a good adsorption capacity (244 mg g−1) at pH 7. On the other hand, Nistico et al. [144] studied the removal of polycyclic aromatic hydrocarbons (PAHs) by using Fe3O4-SBO nanoparticles. They found that a thermal treatment at 550 °C under nitrogen atmosphere of the Fe3O4-SBO nanoparticles enhance their adsorption performance towards PAHs.
Liu et al. [146] developed a synthesis procedure that uses iron mud. This procedure consist of a simple co-precipitation method where iron mud, previously dissolved with 2% HNO3 overnight, acts as an Fe(III) source, and the addition of ascorbic acid (AA) reduces part of the Fe(III) to Fe(II) needed for the formation of magnetite at alkaline conditions. Increasing the AA/Fe3+ ratio during synthesis resulted in increased saturation magnetization values, crystallite size and reduced BET specific area. To further reduce the production cost, acid wastewater from a propylene plant was used to replace nitric acid in digestion of iron mud. Samples with higher crystallite size exhibited less BET specific surface area and less adsorption capacity. Results yield maximum methylene blue adsorption capacities of 87 mg g−1 for the material synthetized with a 0.1 AA/Fe3+ ratio. A list of magnetic waste-based nanomaterials with their adsorption capacity for organic contaminants is summarized in Table 5.
7. Conclusions and Future Perspective Magnetic core–shell nanoparticles and nanocomposites containing iron oxide nanoparticles are a very attractive option to be used in water treatment, due to their advantages in terms of improving some of the properties of unmodified materials for the adsorption of pollutants, namely: (i) a synergistic combination of adsorbent materials where a material is chemically anchored or physically adsorbed on magnetic nanoparticles; (ii) the use of low-cost materials; (iii) facilitation of the separation of the aqueous medium by a simple magnetic process, reducing the overall cost of the process; (iv) the possibility of being reused successively; (v) potential for change in the physicochemical properties of the nanoparticles and nanocomposites surface just by adjusting the experimental conditions, offering a high versatility to be applied to a wide range of contaminants (anionic, cationic, hydrophilic or hydrophobic). Therefore, nanoadsorbents with magnetic response has shown several advantages that could be used in the development water treatment technologies. In this review, the adsorption capacities of magnetic nanomaterials based on silica, clay, carbonaceous materials, polymers and waste were highlighted in order to provide valuable information related to their efficiency of various organic pollutants’ removal. Although magnetic core–shell nanoparticles and magnetic nanocomposites possess different structural characteristics and different removal mechanisms of organic molecules, their adsorption capacities for various organic pollutants are similar. It is worth mentioning that there are some cases where ultra-high adsorption uptake of organic contaminants was achieved. On the other hand, the preparation of nanoadsorbents by combining magnetic iron oxide nanoparticles with materials such as clays, carbon or polymers enable to control the aggregation of the magnetic nanoparticles and improve their performance in aqueous media. Despite the growing interest in the synthesis of magnetic nanoadsorbents for water treatment in last years, nowadays there are few industrial applications and most of the research work is based on small-scale studies. We believe that further studies are needed to address large-scale applications, taking into account design aspects related to stability, adsorbent regeneration, and separation from the aqueous medium. This could help to identify the key operating conditions to achieve low-cost removal of the contaminant with minimal environmental impact. Along with these studies, the efficient production of magnetic nanomaterials at large scale must be investigated further, taking into consideration the environmental impact of manufacturing these materials.
![View Image - Figure 1.(A) TEM image of non-porous silica covering Fe3O4 nanoparticles (reproduced with permission from [36], published by Royal Society of Chemistry, 2015; (B) TEM image of mesoporous-silica covering Fe3O4 nanoparticles (reproduced from [37], published by Royal Society of Chemistry, 2018); (C) SEM images of Raspberry-like' supraparticle system (reproduced with permission from [38], published by ChemNanoMat, 2019); and (D) TEM micrographs of Fe3O4@SiO2@h-mSiO2 (reproduced with permission from [36], published by Royal Society of Chemistry, 2015).](https://media.proquest.com/media/hms/THUM/2/4MU5G?_a=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&_s=ylVWww3Yt1T2BHgLmA9Z462yPWk%3D "View Image - Figure 1.(A) TEM image of non-porous silica covering Fe3O4 nanoparticles (reproduced with permission from [36], published by Royal Society of Chemistry, 2015; (B) TEM image of mesoporous-silica covering Fe3O4 nanoparticles (reproduced from [37], published by Royal Society of Chemistry, 2018); (C) SEM images of Raspberry-like' supraparticle system (reproduced with permission from [38], published by ChemNanoMat, 2019); and (D) TEM micrographs of Fe3O4@SiO2@h-mSiO2 (reproduced with permission from [36], published by Royal Society of Chemistry, 2015).")
Enlarge this image.Figure 1.(A) TEM image of non-porous silica covering Fe3O4 nanoparticles (reproduced with permission from [36], published by Royal Society of Chemistry, 2015; (B) TEM image of mesoporous-silica covering Fe3O4 nanoparticles (reproduced from [37], published by Royal Society of Chemistry, 2018); (C) SEM images of Raspberry-like' supraparticle system (reproduced with permission from [38], published by ChemNanoMat, 2019); and (D) TEM micrographs of Fe3O4@SiO2@h-mSiO2 (reproduced with permission from [36], published by Royal Society of Chemistry, 2015).
Enlarge this image.Figure 2. Scheme of typical synthesis routes to obtain magnetic nanoparticle/clay mineral 2:1 type (MNP/CM) nanocomposites: (A1) pillaring with nonmagnetic pillar; (A2) pillaring with magnetic pillar; (B) coprecipitation; (C1) intercalation of MNP into surfactant intercalated clay mineral; (C2) intercalation of surfactant-modified MNP into clay mineral.
| Adsorbent | Surface Area (m2 g−1) | Magnetic Saturation (emu g−1) | Organic Pollutant | Adsorption Capacity (mg g−1) | Ref. |
|---|---|---|---|---|---|
| Fe3O4@SiO2 | - | 48.06 | Congo red | 50.54 | [33] |
| Fe3O4@SiO2-PVP | 60.82 | 30.89 | Phenanthrene | 18.84 | [34] |
| Fe3O4@SiO2–VTEOS–DMDAAC | - | - | Methylene blue | 109.89 | [41] |
| Fe3O4@SiO2-EDA-COOH | - | 58.7 | Methylene blue | 43.15 | [43] |
| Fe3O4@SiO2@Zn−TDPAT | - | >20 | Methylene blue Congo red | 58.67 17.73 | [56] |
| Fe3O4@SiO2@UiO-67 | - | 20.9 | Glyphosate | 256.54 | [44] |
| Fe@SiO2@PDA | - | 51.98 | Anthracene Phenanthrene | 0.484 0.184 | [35] |
| Fe3O4/SiO2 10 nm SP | 193 | >25 | Methylene blue | 93 | [38] |
| Fe3O4@SiO2-NH2 | - | >40 | Methylene red | 81.39 | [45] |
| Fe3O4@SiO2@mSiO2-CD | 119 | 30.99 | Doxycycline | 78 | [37] |
| Fe3O4@SiO2-C18 | 303 | 22.62 | Methylene blue | 363.64 | [51] |
| γ-Fe2O3@mSiO2-TPODAC | 1.63 | 7.09 | Methyl orange Gemfibrozil Sulfamethoxazole Acenaphtene Phenanthrene | 104 50 50 0.83 0.95 | [52] |
| mMCM-41-g-p(GMA)-TAEA | 185 | 19.6 | Direct blue-6 Direct black-38 | 142.7 79.9 | [54] |
| M-SBA-15/CPAA | 159 | 2.68 | Acid blue 25 | 909.09 | [53] |
| γ-Fe2O3@SiO2@h-mSiO2 | 329 | - | Methylene blue | 41 | [55] |
| MNCM-1 | 576 | 2.9 | Methylene blue | 248 | [57] |
| Adsorbent | Surface Area (m2 g−1) | Magnetic Saturation (emu g−1) | Organic Pollutant | Adsorption Capacity (mg g−1) | Ref. |
|---|---|---|---|---|---|
| Clay:chitosan:PAC:MNP | 95 | 1.91 | Atenolol | 15.6 | [6] |
| Ciprofloxacin | 39.1 | ||||
| Gemfibrozil | 24.8 | ||||
| Fe3O4/Mt | 148 | - | Methylene blue | 106.4 | [4] |
| Magnetic chitosan/clay beads | - | - | Methylene blue | 82 | [3] |
| MSEP | 112 | 31.8 | Atrazine | 1.79 | [67] |
| MHNTs | - | 42.87 | Norfloxacin | 99.6 | [68] |
| Fe3O4/kaolin | 32 | 12.32 | Direct red 23 | 22.88 | [10] |
| Fe3O4-Sep | 81 | 26.22 | Bisphenol A | - | [66] |
| BMF-1 | - | - | Methylene blue | 14.93 | [11] |
| BMF-0.5 | - | - | Methylene blue | 12.35 | [11] |
| Mt/PANI/Fe3O4-2 | - | 36.52 | Methylene blue | 184.5 | [69] |
| Adsorbent | Surface Area (m2 g−1) | Magnetic Saturation (emu g−1) | Organic Pollutant | Adsorption Capacity (mg g−1) | Ref. |
|---|---|---|---|---|---|
| Bio-magnetic membrane capsules from PVA–alginate matrix | - | 11.02 | Malachite green | 500 | [123] |
| Magnetic nanocellulose from olive industry solid waste | - | 21.4 | Methylene blue | 166.67 | [124] |
| Fe3O4-amine-functionalized chitosan with p-Benzoquinone | - | 17.5 | Diclofenac sodium | 469.48 | [125] |
| Magnetic β-cyclodextrin porous polymer nanospheres | 70.63 | 44.8 | Methylene blue | 305.8 | [94] |
| Magnetic porphyrin-based porous organic polymer | 310 | 45.9 | Phenylurea herbicides | Metoxuron = 1.13, Mono-linuron = 0.95, Chlorotoluron = 0.86, Buturon = 1.10 | [92] |
| Magnetic copper based metal–organic frameworks (MOF) | 327.9 | 44 | Fluoroquinolone antibiotics | Ciprofloxacin= 538 Norfloxacin =513 | [106] |
| Magnetic polyimide-Mg-Fe layered double hydroxides core–shell composite | 26.38 | Tetracycline 2,4-dichlorophenol Glyphosate | 185.53 176.06 190.84 | [126] | |
| Magnetic mesoporous lignin from date palm pits | 640 | 37.81 | Diesel Gasoline | Diesel = 22370 Gasoil = 21010 | [127] |
| Adsorbent | Surface Area (m g−1) | Magnetic Saturation (emu g−1) | Organic Pollutant | Adsorption Capacity (mg g−1) | Ref. |
|---|---|---|---|---|---|
| Magnetic Sawdust | - | - | Crystal violet | 51.2 | [132] |
| Magnetic Peanut husk | - | - | Acridine orange Bismark brown Crystal violet Safranin O | 71.4 95.3 80.9 86.1 | [133] |
| Fe3O4-Coffe Skin | - | - | Methylene blue | 556 | [134] |
| Fe3O4-Ground coffe waste | - | - | Methylene blue | 128 | [135] |
| Fe3O4-Starch Fe3O4-Av1-Starch Fe3O4-Wm-Starch | 62 78 63 | 51 43 49 | Optilan blue | 119 111 63 | [136] |
| Fe3O4-Red mud | 84 | 12 | Diazinon Malathion Parathiion Chlorpyrifos | 1.9 1.7 2.9 3.9 | [137] |
| Fe3O4-Red mud | 84 | 12 | Ciprofloxacin | 200 | [138] |
| Fe3O4-Tea Waste | - | - | Neutral red Reactive blue Congo red Janus green Methilene blue Crystal violet Thionine | 127 88 83 130 119 114 128 | [139] |
| Fe3O4-Tree leaves | - | - | Malachite green Neutral red Methylene blue Crystal violet Methyl violet | 89 101 128 117 133 | [140] |
| Fe3O4-Olive cristal cellulose | - | 21 | Methylene blue | 166 | [124] |
| Fe3O4-Acuatic Plant | 7 | 3 | Methylene blue | 474 | [141] |
| Fe3O4-Beer Yeast | - | - | Methylene blue Basic violet | 609 521 | [142] |
| Fe3O4-SBO | 35 | 51 | Crystal violet | 244 | [143] |
| Fe3O4 (MP-10) | 70 | 9 | Methylene blue | 99.4 | [144] |
| Fe3O4 (MP-3) Fe3O4 (MP-3w) | 176 119 | 5 4 | Methylene blue | 87.3 56.7 | [146] |
Author Contributions
Conceptualization, L.C.; Investigation, M.E.P. (Marcos E. Peralta), S.O., I.G.F., F.O.M., M.E.P. (María E. Parolo) and L.C.; Writing-Original Draft Preparation, M.E.P. (Marcos E. Peralta), S.O., I.G.F., F.O.M., M.E.P. (María E. Parolo) and L.C.; Writing-Review & Editing, L.C.; Visualization, L.C.; Supervision, M.E.P. (María E. Parolo) and L.C.; Project Administration, M.E.P. (María E. Parolo) and L.C.; Funding Acquisition, M.E.P. (María E. Parolo) and L.C. All authors have read and agreed to the published version of the manuscript.
Funding
The authors acknowledge financial support from CONICET (PUE0067), ANPCyT (PICT 2017-1847) and the Universidad Nacional del Comahue (UNCo-04/I217). M.E.P., F.O.M. and S.O. thank CONICET for their research graduate grants. L.C. is research member of CONICET.
Conflicts of Interest
The authors declare no conflict of interest.
1. European Environment Agency. European Waters Assessment of Status and Pressures 2018; EEA Report; European Environment Agency: Luxembourg, 2018; ISBN 9789292139476.
2. Stuart, M.; Lapworth, D.; Crane, E.; Hart, A. Review of risk from potential emerging contaminants in UK groundwater. Sci. Total Environ. 2012, 416, 1-21.
3. Bée, A.; Obeid, L.; Mbolantenaina, R.; Welschbillig, M.; Talbot, D. Magnetic chitosan/clay beads: A magsorbent for the removal of cationic dye from water. J. Magn. Magn. Mater. 2017, 421, 59-64.
4. Chang, J.; Ma, J.; Ma, Q.; Zhang, D.; Qiao, N.; Hu, M.; Ma, H. Adsorption of methylene blue onto Fe3O4/activated montmorillonite nanocomposite. Appl. Clay Sci. 2016, 119, 132-140.
5. Han, H.; Rafiq, M.K.; Zhou, T.; Xu, R.; Mašek, O.; Li, X. A critical review of clay-based composites with enhanced adsorption performance for metal and organic pollutants. J. Hazard. Mater. 2019, 369, 780-796.
6. Arya, V.; Philip, L. Adsorption of pharmaceuticals in water using Fe3O4 coated polymer clay composite. Microporous Mesoporous Mater. 2016, 232, 273-280.
7. Nagy, Z.M.; Molnár, M.; Fekete-Kertész, I.; Molnár-Perl, I.; Fenyvesi, É.; Gruiz, K. Removal of emerging micropollutants from water using cyclodextrin. Sci. Total Environ. 2014, 485, 711-719.
8. Yang, K.; Wu, W.; Jing, Q.; Zhu, L. Aqueous adsorption of aniline, phenol, and their substitutes by multi-walled carbon nanotubes. Environ. Sci. Technol. 2008, 42, 7931-7936.
9. Dailianis, S.; Tsarpali, V.; Melas, K.; Karapanagioti, H.K.; Manariotis, I.D. Aqueous phenanthrene toxicity after high-frequency ultrasound degradation. Aquat. Toxicol. 2014, 147, 32-40.
10. Magdy, A.; Fouad, Y.O.; Abdel-Aziz, M.H.; Konsowa, A.H. Synthesis and characterization of Fe3O4/kaolin magnetic nanocomposite and its application in wastewater treatment. J. Ind. Eng. Chem. 2017, 56, 299-311.
11. Diagboya, P.N.; Dikio, E.D. Scavenging of aqueous toxic organic and inorganic cations using novel facile magneto-carbon black-clay composite adsorbent. J. Clean. Prod. 2018, 180, 71-80.
12. Reddy, D.H.K.; Yun, Y.S. Spinel ferrite magnetic adsorbents: Alternative future materials for water purification? Coord. Chem. Rev. 2016, 315, 90-111.
13. Mehta, D.; Mazumdar, S.; Singh, S.K. Magnetic adsorbents for the treatment of water/wastewater-A review. J. Water Process Eng. 2015, 7, 244-265.
14. Gómez-Pastora, J.; Bringas, E.; Ortiz, I. Recent progress and future challenges on the use of high performance magnetic nano-adsorbents in environmental applications. Chem. Eng. J. 2014, 256, 187-204.
15. Larraza, I.; López-gónzalez, M.; Corrales, T.; Marcelo, G. Hybrid materials: Magnetite-Polyethylenimine-Montmorillonite, as magnetic adsorbents for Cr(VI) water treatment. J. Colloid Interface Sci. 2012, 385, 24-33.
16. Nisticò, R.; Cesano, F.; Garello, F. Magnetic Materials and Systems: Domain structure visualization and other characterization techniques for the application in the materials science and biomedicine. Inorganics 2020, 8, 6.
17. Nisticò, R. Magnetic materials and water treatments for a sustainable future. Res. Chem. Intermed. 2017, 43, 6911-6949.
18. Chen, L.; Zhou, C.H.; Fiore, S.; Tong, D.S.; Zhang, H.; Li, C.S.; Ji, S.F.; Yu, W.H. Functional magnetic nanoparticle/clay mineral nanocomposites: Preparation, magnetism and versatile applications. Appl. Clay Sci. 2016, 127, 143-163.
19. Yuan, P.; Fan, M.; Yang, D.; He, H.; Liu, D.; Yuan, A.; Zhu, J.X.; Chen, T.H. Montmorillonite-supported magnetite nanoparticles for the removal of hexavalent chromium [Cr(VI)] from aqueous solutions. J. Hazard. Mater. 2009, 166, 821-829.
20. Mohammed, L.; Gomaa, H.G.; Ragab, D.; Zhu, J. Magnetic nanoparticles for environmental and biomedical applications: A review. Particuology 2017, 30, 1-14.
21. Liu, J.; Qiao, S.Z.; Hu, Q.H.; Lu, G.Q. Magnetic nanocomposites with mesoporous structures: Synthesis and applications. Small 2011, 7, 425-443.
22. Tang, S.C.N.; Lo, I.M.C. Magnetic nanoparticles: Essential factors for sustainable environmental applications. Water Res. 2013, 47, 2613-2632.
23. Gao, F. An Overview of Surface-Functionalized Magnetic Nanoparticles: Preparation and Application for Wastewater Treatment. ChemistrySelect 2019, 4, 6805-6811.
24. Gómez-Pastora, J.; Dominguez, S.; Bringas, E.; Rivero, M.J.; Ortiz, I.; Dionysiou, D.D. Review and perspectives on the use of magnetic nanophotocatalysts (MNPCs) in water treatment. Chem. Eng. J. 2017, 310, 407-427.
25. Sharma, R.K.; Sharma, S.; Dutta, S.; Zboril, R.; Gawande, M.B. Silica-nanosphere-based organic-inorganic hybrid nanomaterials: Synthesis, functionalization and applications in catalysis. Green Chem. 2015, 17, 3207-3230.
26. Cashin, V.B.; Eldridge, D.S.; Yu, A.; Zhao, D. Surface functionalization and manipulation of mesoporous silica adsorbents for improved removal of pollutants: A review. Environ. Sci. Water Res. Technol. 2018, 4, 110-128.
27. Walcarius, A.; Mercier, L. Mesoporous organosilica adsorbents: Nanoengineered materials for removal of organic and inorganic pollutants. J. Mater. Chem. 2010, 20, 4478-4511.
28. Wan, Y.; Zhao, D. On the Controllable Soft-Templating Approach to Mesoporous Silicates. Chem. Rev. 2007, 107, 2821-2860.
29. Slowing, I.I.; Vivero-Escoto, J.L.; Trewyn, B.G.; Lin, V.S.Y. Mesoporous silica nanoparticles: Structural design and applications. J. Mater. Chem. 2010, 20, 7924-7937.
30. Li, R.; Zhang, L.; Wang, P. Rational design of nanomaterials for water treatment. Nanoscale 2015, 7, 17167-17194.
31. Diagboya, P.N.E.; Dikio, E.D. Silica-based mesoporous materials; emerging designer adsorbents for aqueous pollutants removal and water treatment. Microporous Mesoporous Mater. 2018, 266, 252-267.
32. Cendrowski, K.; Sikora, P.; Zielinska, B.; Horszczaruk, E.; Mijowska, E. Chemical and thermal stability of core-shelled magnetite nanoparticles and solid silica. Appl. Surf. Sci. 2017, 407, 391-397.
33. Wang, P.; Wang, X.; Yu, S.; Zou, Y.; Wang, J.; Chen, Z.; Alharbi, N.S.; Alsaedi, A.; Hayat, T.; Chen, Y.; et al. Silica coated Fe3O4 magnetic nanospheres for high removal of organic pollutants from wastewater. Chem. Eng. J. 2016, 306, 280-288.
34. Wang, L.; Shen, C.; Cao, Y. PVP modified Fe3O4@SiO2 nanoparticles as a new adsorbent for hydrophobic substances. J. Phys. Chem. Solids 2019, 133, 28-34.
35. Li, J.; Zhou, Q.; Liu, Y.; Lei, M. Recyclable nanoscale zero-valent iron-based magnetic polydopamine coated nanomaterials for the adsorption and removal of phenanthrene and anthracene. Sci. Technol. Adv. Mater. 2017, 18, 3-16.
36. Yue, Q.; Zhang, Y.; Wang, C.; Wang, X.; Sun, Z.; Hou, X.F.; Zhao, D.; Deng, Y. Magnetic yolk-shell mesoporous silica microspheres with supported Au nanoparticles as recyclable high-performance nanocatalysts. J. Mater. Chem. A 2015, 3, 4586-4594.
37. Zhang, Y.; Jiang, F.; Huang, D.; Hou, S. A facile route to magnetic mesoporous core-shell structured silicas containing covalently bound cyclodextrins for the removal of the antibiotic doxycycline from water. RSC Adv. 2018, 8, 31348-31357.
38. Oppmann, M.; Wozar, M.; Reichstein, J.; Mandel, K. Reusable Superparamagnetic Raspberry-Like Supraparticle Adsorbers as Instant Cleaning Agents for Ultrafast Dye Removal from Water. ChemNanoMat 2019, 5, 230-240.
39. Hoffmann, F.; Cornelius, M.; Morell, J.; Fröba, M. Silica-based mesoporous organic-inorganic hybrid materials. Angew. Chem. Int. Ed. 2006, 45, 3216-3251.
40. Sasaki, T.; Tanaka, S. Adsorption behavior of some aromatic compounds on hydrophobic magnetite for magnetic separation. J. Hazard. Mater. 2011, 196, 327-334.
41. Chen, J.; Chen, H. Removal of anionic dyes from an aqueous solution by a magnetic cationic adsorbent modified with DMDAAC. New J. Chem. 2018, 42, 7262-7271.
42. Peralta, M.E.; Jadhav, S.A.; Magnacca, G.; Scalarone, D.; Mártire, D.O.; Parolo, M.E.; Carlos, L. Synthesis and in vitro testing of thermoresponsive polymer-grafted core-shell magnetic mesoporous silica nanoparticles for efficient controlled and targeted drug delivery. J. Colloid Interface Sci. 2019, 544, 198-205.
43. Jiaqi, Z.; Yimin, D.; Danyang, L.; Shengyun, W.; Liling, Z.; Yi, Z. Synthesis of carboxyl-functionalized magnetic nanoparticle for the removal of methylene blue. Colloids Surf. A Physicochem. Eng. Asp. 2019, 572, 58-66.
44. Yang, Q.; Wang, J.; Chen, X.; Yang, W.; Pei, H.; Hu, N.; Li, Z.; Suo, Y.; Li, T.; Wang, J. The simultaneous detection and removal of organophosphorus pesticides by a novel Zr-MOF based smart adsorbent. J. Mater. Chem. A 2018, 6, 2184-2192.
45. Ghorbani, F.; Kamari, S. Core-shell magnetic nanocomposite of Fe3O4@SiO2 @NH2 as an efficient and highly recyclable adsorbent of methyl red dye from aqueous environments. Environ. Technol. Innov. 2019, 14, 100333.
46. Peres, E.C.; Slaviero, J.C.; Cunha, A.M.; Hosseini-Bandegharaei, A.; Dotto, G.L. Microwave synthesis of silica nanoparticles and its application for methylene blue adsorption. J. Environ. Chem. Eng. 2018, 6, 649-659.
47. Liu, S.; Chen, X.; Ai, W.; Wei, C. A new method to prepare mesoporous silica from coal gasification fine slag and its application in methylene blue adsorption. J. Clean. Prod. 2019, 212, 1062-1071.
48. Brigante, M.; Parolo, M.E.; Schulz, P.C.; Avena, M. Synthesis, characterization of mesoporous silica powders and application to antibiotic remotion from aqueous solution. Effect of supported Fe-oxide on the SiO2 adsorption properties. Powder Technol. 2014, 253, 178-186.
49. Saikia, D.; Deka, J.R.; Wu, C.E.; Yang, Y.C.; Kao, H.M. pH responsive selective protein adsorption by carboxylic acid functionalized large pore mesoporous silica nanoparticles SBA-1. Mater. Sci. Eng. C 2019, 94, 344-356.
50. Ganiyu, S.O.; Bispo, C.; Bion, N.; Ferreira, P.; Batonneau-Gener, I. Periodic Mesoporous Organosilicas as adsorbents for the organic pollutants removal in aqueous phase. Microporous Mesoporous Mater. 2014, 200, 117-123.
51. Zhang, X.; Zeng, T.; Wang, S.; Niu, H.; Wang, X.; Cai, Y. One-pot synthesis of C18-functionalized core-shell magnetic mesoporous silica composite as efficient sorbent for organic dye. J. Colloid Interface Sci. 2015, 448, 189-196.
52. Huang, Y.; Fulton, A.N.; Keller, A.A. Optimization of porous structure of superparamagnetic nanoparticle adsorbents for higher and faster removal of emerging organic contaminants and PAHs. Environ. Sci. Water Res. Technol. 2016, 2, 521-528.
53. Ghanei, M.; Rashidi, A.; Tayebi, H.; Yazdanshenas, M.E. Removal of Acid Blue 25 from Aqueous Media by Magnetic-SBA-15/CPAA Super Adsorbent: Adsorption Isotherm, Kinetic, and Thermodynamic Studies. J. Chem. Eng. Data 2018, 63, 3592-3605.
54. Arica, T.A.; Ayas, E.; Arica, M.Y. Magnetic MCM-41 silica particles grafted with poly(glycidylmethacrylate) brush: Modification and application for removal of direct dyes. Microporous Mesoporous Mater. 2017, 243, 164-175.
55. Jin, C.; Wang, Y.; Tang, H.; Zhu, K.; Liu, X.; Wang, J. Versatile rattle-type magnetic mesoporous silica spheres, working as adsorbents and nanocatalyst containers. J. Sol-Gel Sci. Technol. 2016, 77, 279-287.
56. Wo, R.; Li, Q.L.; Zhu, C.; Zhang, Y.; Qiao, G.F.; Lei, K.Y.; Du, P.; Jiang, W. Preparation and Characterization of Functionalized Metal-Organic Frameworks with Core/Shell Magnetic Particles (Fe3O4@SiO2@MOFs) for Removal of Congo Red and Methylene Blue from Water Solution. J. Chem. Eng. Data 2019, 64, 2455-2463.
57. Kittappa, S.; Pichiah, S.; Kim, J.R.; Yoon, Y.; Snyder, S.A.; Jang, M. Magnetised nanocomposite mesoporous silica and its application for effective removal of methylene blue from aqueous solution. Sep. Purif. Technol. 2015, 153, 67-75.
58. Zhou, Y.; Lu, J.; Zhou, Y.; Liu, Y. Recent advances for dyes removal using novel adsorbents: A review. Environ. Pollut. 2019, 252, 352-365.
59. Musso, T.B.; Parolo, M.E.; Pettinari, G.; Francisca, F.M. Cu(II) and Zn(II) adsorption capacity of three different clay liner materials. J. Environ. Manag. 2014, 146, 50-58.
60. Betega de Paiva, L.; Rita, A.; Valenzuela, F.R. Organoclays: Properties, preparation and applications. Appl. Clay Sci. 2008, 42, 8-24.
61. Parolo, M.E.; Pettinari, G.R.; Musso, T.B.; Sánchez-Izquierdo, M.P.; Fernández, L.G. Characterization of organo-modified bentonite sorbents: The effect of modification conditions on adsorption performance. Appl. Surf. Sci. 2014, 320, 356-363.
62. Naranjo Pablo, M.; Sham Edgardo, L.; Rodriguez, C.E.; Torres Sánchez, R.M.; Monica, F. Identification and quantification of the interaction mechanisms between the cationic surfactant HDTMA-Br and montmorillonite. Clays Clay Miner. 2013, 61, 98-106.
63. Roca Jalil, M.E.; Vieira, R.S.; Azevedo, D.; Baschini, M.; Sapag, K. Improvement in the adsorption of thiabendazole by using aluminum pillared clays. Appl. Clay Sci. 2013, 71, 55-63.
64. Guégan, R. Organoclay applications and limits in the environment. C. R. Chim. 2018, 22, 132-141.
65. Jaber, M.; Miehé-Brendlé, J. Organoclays. Preparation, Properties and Applications. In Ordered Porous Solids; Elsevier: Amsterdam, The Netherlands, 2009; pp. 31-49.
66. Xu, X.; Chen, W.; Zong, S.; Ren, X.; Liu, D. Magnetic clay as catalyst applied to organics degradation in a combined adsorption and Fenton-like process. Chem. Eng. J. 2019, 373, 140-149.
67. Liu, H.; Chen, W.; Liu, C.; Liu, Y.; Dong, C. Magnetic mesoporous clay adsorbent: Preparation, characterization and adsorption capacity for atrazine. Microporous Mesoporous Mater. 2014, 194, 72-78.
68. Fizir, M.; Dramou, P.; Zhang, K.; Sun, C.; Pham-Huy, C.; He, H. Polymer grafted-magnetic halloysite nanotube for controlled and sustained release of cationic drug. J. Colloid Interface Sci. 2017, 505, 476-488.
69. Mu, B.; Tang, J.; Zhang, L.; Wang, A. Preparation, characterization and application on dye adsorption of a well-defined two-dimensional superparamagnetic clay/polyaniline/Fe3O4 nanocomposite. Appl. Clay Sci. 2016, 132, 7-16.
70. Khajeh, M.; Laurent, S.; Dastafkan, K. Nanoadsorbents: Classification, preparation, and applications (with emphasis on aqueous media). Chem. Rev. 2013, 113, 7728-7768.
71. Sherlala, A.I.A.; Raman, A.A.A.; Bello, M.M.; Asghar, A. A review of the applications of organo-functionalized magnetic graphene oxide nanocomposites for heavy metal adsorption. Chemosphere 2018, 193, 1004-1017.
72. Zhu, M.; Diao, G. Review on the progress in synthesis and application of magnetic carbon nanocomposites. Nanoscale 2011, 3, 2748-2767.
73. Boruah, P.K.; Sharma, B.; Hussain, N.; Das, M.R. Magnetically recoverable Fe3O4/graphene nanocomposite towards efficient removal of triazine pesticides from aqueous solution: Investigation of the adsorption phenomenon and specific ion effect. Chemosphere 2017, 168, 1058-1067.
74. Hu, X.; Liu, J.; Mayer, P.; Jiang, G. Impacts of some environmentally relevant parameters on the sorption of polycyclic aromatic hydrocarbons to aqueous suspensions of fullerene. Environ. Toxicol. Chem. 2008, 27, 1868-1874.
75. Yang, K.; Wang, X.; Zhu, L.; Xing, B. Competitive sorption of pyrene, phenanthrene, and naphthalene on multiwalled carbon nanotubes. Environ. Sci. Technol. 2006, 40, 5804-5810.
76. Yang, X.; Li, J.; Wen, T.; Ren, X.; Huang, Y.; Wang, X. Colloids and Surfaces A: Physicochemical and Engineering Aspects Adsorption of naphthalene and its derivatives on magnetic graphene composites and the mechanism investigation. Colloids Surf. A Physicochem. Eng. Asp. 2013, 422, 118-125.
77. Fan, L.; Luo, C.; Sun, M.; Qiu, H.; Li, X. Synthesis of magnetic β-cyclodextrin-chitosan/graphene oxide as nanoadsorbent and its application in dye adsorption and removal. Colloids Surf. B Biointerfaces 2013, 103, 601-607.
78. Ai, L.; Zhang, C.; Chen, Z. Removal of methylene blue from aqueous solution by a solvothermal-synthesized graphene/magnetite composite. J. Hazard. Mater. 2011, 192, 1515-1524.
79. Eom, D.; Prezzi, D.; Rim, K.T.; Zhou, H.; Lefenfeld, M.; Xiao, S.; Nuckolls, C.; Hybertsen, M.S.; Heinz, T.F.; Flynn, G.W. Structure and electronic properties of graphene nanoislands on CO(0001). Nano Lett. 2009, 9, 2844-2848.
80. Ramesha, G.K.; Vijaya Kumara, A.; Muralidhara, H.B.; Sampath, S. Graphene and graphene oxide as effective adsorbents toward anionic and cationic dyes. J. Colloid Interface Sci. 2011, 361, 270-277.
81. Yu, B.; Zhang, X.; Xie, J.; Wu, R.; Liu, X.; Li, H.; Chen, F.; Yang, H.; Ming, Z.; Yang, S.-T. Magnetic graphene sponge for the removal of methylene blue. Appl. Surf. Sci. 2015, 351, 765-771.
82. Alizadeh Fard, M.; Barkdoll, B. Using recyclable magnetic carbon nanotube to remove micropollutants from aqueous solutions. J. Mol. Liq. 2018, 249, 193-202.
83. Gong, J.L.; Wang, B.; Zeng, G.M.; Yang, C.P.; Niu, C.G.; Niu, Q.Y.; Zhou, W.J.; Liang, Y. Removal of cationic dyes from aqueous solution using magnetic multi-wall carbon nanotube nanocomposite as adsorbent. J. Hazard. Mater. 2009, 164, 1517-1522.
84. Zhao, Y.; Chen, H.; Li, J.; Chen, C. Hierarchical MWCNTs/Fe3O4/PANI magnetic composite as adsorbent for methyl orange removal. J. Colloid Interface Sci. 2015, 450, 189-195.
85. Deng, Y.; Ok, Y.S.; Mohan, D.; Pittman, C.U.; Dou, X. Carbamazepine removal from water by carbon dot-modified magnetic carbon nanotubes. Environ. Res. 2019, 169, 434-444.
86. Liu, X.; Tian, J.; Li, Y.; Sun, N.; Mi, S.; Xie, Y.; Chen, Z. Enhanced dyes adsorption from wastewater via Fe3O4 nanoparticles functionalized activated carbon. J. Hazard. Mater. 2019, 373, 397-407.
87. Shan, D.; Deng, S.; Zhao, T.; Wang, B.; Wang, Y.; Huang, J.; Yu, G.; Winglee, J.; Wiesner, M.R. Preparation of ultrafine magnetic biochar and activated carbon for pharmaceutical adsorption and subsequent degradation by ball milling. J. Hazard. Mater. 2016, 305, 156-163.
88. Yu, B.; Bai, Y.; Ming, Z.; Yang, H.; Chen, L.; Hu, X.; Feng, S.; Yang, S.T. Adsorption behaviors of tetracycline on magnetic graphene oxide sponge. Mater. Chem. Phys. 2017, 198, 283-290.
89. Lompe, K.M.; Vo Duy, S.; Peldszus, S.; Sauvé, S.; Barbeau, B. Removal of micropollutants by fresh and colonized magnetic powdered activated carbon. J. Hazard. Mater. 2018, 360, 349-355.
90. Alaba, P.A.; Oladoja, N.A.; Sani, Y.M.; Ayodele, O.B.; Mohammed, I.Y.; Olupinla, S.F.; Daud, W.M.W. Insight into wastewater decontamination using polymeric adsorbents. J. Environ. Chem. Eng. 2018, 6, 1651-1672.
91. Lv, S.W.; Liu, J.M.; Wang, Z.H.; Ma, H.; Li, C.Y.; Zhao, N.; Wang, S. Recent advances on porous organic frameworks for the adsorptive removal of hazardous materials. J. Environ. Sci. 2019, 80, 169-185.
92. Zhou, Q.; Wang, Y.; Xiao, J.; Fan, H.; Chen, C. Preparation and characterization of magnetic nanomaterial and its application for removal of polycyclic aromatic hydrocarbons. J. Hazard. Mater. 2019, 371, 323-331.
93. Huo, Y.; Wu, H.; Wang, Z.; Wang, F.; Liu, Y.; Feng, Y.; Zhao, Y. Preparation of core/shell nanocomposite adsorbents based on amine polymer-modified magnetic materials for the efficient adsorption of anionic dyes. Colloids Surf. A Physicochem. Eng. Asp. 2018, 549, 174-183.
94. Liu, D.; Huang, Z.; Li, M.; Sun, P.; Yu, T.; Zhou, L. Novel porous magnetic nanospheres functionalized by β-cyclodextrin polymer and its application in organic pollutants from aqueous solution. Environ. Pollut. 2019, 250, 639-649.
95. Budd, P.M.; Ghanem, B.S.; Makhseed, S.; McKeown, N.B.; Msayib, K.J.; Tattershall, C.E. Polymers of intrinsic microporosity (PIMs): Robust, solution-processable, organic nanoporous materials. Chem. Commun. 2004, 4, 230-231.
96. Kumar, P.; Bansal, V.; Kim, K.H.; Kwon, E.E. Metal-organic frameworks (MOFs) as futuristic options for wastewater treatment. J. Ind. Eng. Chem. 2018, 62, 130-145.
97. Han, S.S.; Furukawa, H.; Yaghi, O.M.; Iii, W.A.G. Covalent organic frameworks as exceptional hydrogen storage materials. J. Am. Chem. Soc. 2008, 105, 11580-11581.
98. Ben, T.; Ren, H.; Shengqian, M.; Cao, D.; Lan, J.; Jing, X.; Wang, W.; Xu, J.; Deng, F.; Simmons, J.M.; et al. Targeted synthesis of a porous aromatic framework with high stability and exceptionally high surface area. Angew. Chem. Int. Ed. 2009, 48, 9457-9460.
99. Germain, J.; Hradil, J.; Fréchet, J.M.J.; Svec, F. High surface area nanoporous polymers for reversible hydrogen storage. Chem. Mater. 2006, 18, 4430-4435.
100. Hu, A.; Yang, X.; You, Q.; Liu, Y.; Wang, Q.; Liao, G.; Wang, D. Magnetically hyper-cross-linked polymers with well-developed mesoporous: A broad-spectrum and highly efficient adsorbent for water purification. J. Mater. Sci. 2019, 54, 2712-2728.
101. Li, J.; Liu, Y.; Ai, Y.; Alsaedi, A.; Hayat, T.; Wang, X. Combined experimental and theoretical investigation on selective removal of mercury ions by metal organic frameworks modified with thiol groups. Chem. Eng. J. 2018, 354, 790-801.
102. Wang, C.; Liu, X.; Keser Demir, N.; Chen, J.P.; Li, K. Applications of water stable metal-organic frameworks. Chem. Soc. Rev. 2016, 45, 5107-5134.
103. Safaei, M.; Foroughi, M.M.; Ebrahimpoor, N.; Jahani, S.; Omidi, A.; Khatami, M. A review on metal-organic frameworks: Synthesis and applications. TrAC Trends Anal. Chem. 2019, 118, 401-425.
104. Yang, Q.; Ren, S.S.; Zhao, Q.; Lu, R.; Hang, C.; Chen, Z.; Zheng, H. Selective separation of methyl orange from water using magnetic ZIF-67 composites. Chem. Eng. J. 2018, 333, 49-57.
105. Hamedi, A.; Zarandi, M.B.; Nateghi, M.R. Highly efficient removal of dye pollutants by MIL-101(Fe) metal-organic framework loaded magnetic particles mediated by Poly L-Dopa. J. Environ. Chem. Eng. 2019, 7, 102882.
106. Wu, G.; Ma, J.; Li, S.; Guan, J.; Jiang, B.; Wang, L.; Li, J.; Wang, X.; Chen, L. Magnetic copper-based metal organic framework as an effective and recyclable adsorbent for removal of two fluoroquinolone antibiotics from aqueous solutions. J. Colloid Interface Sci. 2018, 528, 360-371.
107. Han, S.S.; Mendoza-Cortés, J.L.; Goddard, W.A. Recent advances on simulation and theory of hydrogen storage in metal-organic frameworks and covalent organic frameworks. Chem. Soc. Rev. 2009, 38, 1460-1476.
108. Fernandes, S.P.S.; Romero, V.; Espiña, B.; Salonen, L.M. Tailoring Covalent Organic Frameworks to Capture Water Contaminants. Chem. A Eur. J. 2019, 25, 6461-6473.
109. Li, Y.; Zhang, H.; Chen, Y.; Huang, L.; Lin, Z.; Cai, Z. Core-Shell Structured Magnetic Covalent Organic Framework Nanocomposites for Triclosan and Triclocarban Adsorption. ACS Appl. Mater. Interfaces 2019, 11, 22492-22500.
110. Li, Y.; Yang, C.X.; Yan, X.P. Controllable preparation of core-shell magnetic covalent-organic framework nanospheres for efficient adsorption and removal of bisphenols in aqueous solution. Chem. Commun. 2017, 53, 2511-2514.
111. He, S.; Zeng, T.; Wang, S.; Niu, H.; Cai, Y. Facile synthesis of magnetic covalent organic framework with three-dimensional bouquet-like structure for enhanced extraction of organic targets. ACS Appl. Mater. Interfaces 2017, 9, 2959-2965.
112. Wang, B.; Wan, Y.; Zheng, Y.; Lee, X.; Liu, T.; Yu, Z.; Huang, J.; Ok, Y.S.; Chen, J.; Gao, B. Alginate-based composites for environmental applications: A critical review. Crit. Rev. Environ. Sci. Technol. 2019, 49, 318-356.
113. Lee, K.Y.; Rowley, J.A.; Eiselt, P.; Moy, E.M.; Bouhadir, K.H.; Mooney, D.J. Controlling mechanical and swelling properties of alginate hydrogels independently by cross-linker type and cross-linking density. Macromolecules 2000, 33, 4291-4294.
114. Urquiza, T.K.V.; Pérez, O.P.; Saldaña, M.G. Effect of the cross-linking with calcium ions on the structural and thermo-mechanical properties of alginate films. Mater. Res. Soc. Symp. Proc. 2011, 1355, 16-21.
115. Talbot, D.; Abramson, S.; Griffete, N.; Bée, A. pH-sensitive magnetic alginate/γ-Fe2O3 nanoparticles for adsorption/desorption of a cationic dye from water. J. Water Process Eng. 2018, 25, 301-308.
116. Mohammadi, A.; Daemi, H.; Barikani, M. Fast removal of malachite green dye using novel superparamagnetic sodium alginate-coated Fe3O4 nanoparticles. Int. J. Biol. Macromol. 2014, 69, 447-455.
117. Wen, Y.; Shen, C.; Ni, Y.; Tong, S.; Yu, F. Glow discharge plasma in water: A green approach to enhancing ability of chitosan for dye removal. J. Hazard. Mater. 2012, 201, 162-169.
118. Li, T.T.; Liu, Y.G.; Peng, Q.Q.; Hu, X.J.; Liao, T.; Wang, H.; Lu, M. Removal of lead(II) from aqueous solution with ethylenediamine-modified yeast biomass coated with magnetic chitosan microparticles: Kinetic and equilibrium modeling. Chem. Eng. J. 2013, 214, 189-197.
119. Park, S.I.; Kwak, I.S.; Won, S.W.; Yun, Y.S. Glutaraldehyde-crosslinked chitosan beads for sorptive separation of Au(III) and Pd(II): Opening a way to design reduction-coupled selectivity-tunable sorbents for separation of precious metals. J. Hazard. Mater. 2013, 248, 211-218.
120. Tirtom, V.N.; Dinçer, A.; Becerik, S.; Aydemir, T.; Çelik, A. Comparative adsorption of Ni(II) and Cd(II) ions on epichlorohydrin crosslinked chitosan-clay composite beads in aqueous solution. Chem. Eng. J. 2012, 197, 379-386.
121. Zheng, C.; Zheng, H.; Wang, Y.; Sun, Y.; An, Y.; Liu, H.; Liu, S. Modified magnetic chitosan microparticles as novel superior adsorbents with huge "force field" for capturing food dyes. J. Hazard. Mater. 2019, 367, 492-503.
122. Xu, B.; Zheng, C.; Zheng, H.; Wang, Y.; Zhao, C.; Zhao, C.; Zhang, S. Polymer-grafted magnetic microspheres for enhanced removal of methylene blue from aqueous solutions. RSC Adv. 2017, 7, 47029-47037.
123. Ali, I.; Peng, C.; Naz, I.; Lin, D.; Saroj, D.P.; Ali, M. Development and application of novel bio-magnetic membrane capsules for the removal of the cationic dye malachite green in wastewater treatment. RSC Adv. 2019, 9, 3625-3646.
124. Jodeh, S.; Hamed, O.; Melhem, A.; Salghi, R.; Jodeh, D.; Azzaoui, K.; Benmassaoud, Y.; Murtada, K. Magnetic nanocellulose from olive industry solid waste for the effective removal of methylene blue from wastewater. Environ. Sci. Pollut. Res. 2018, 25, 22060-22074.
125. Liang, X.X.; Omer, A.M.; Hu, Z.H.; Wang, Y.G.; Yu, D.; Ouyang, X.K. Efficient adsorption of diclofenac sodium from aqueous solutions using magnetic amine-functionalized chitosan. Chemosphere 2019, 217, 270-278.
126. Wu, H.; Zhang, H.; Zhang, W.; Yang, X.; Zhou, H.; Pan, Z.; Wang, D. Preparation of magnetic polyimide@ Mg-Fe layered double hydroxides core-shell composite for effective removal of various organic contaminants from aqueous solution. Chemosphere 2019, 219, 66-75.
127. Ahamad, T.; Naushad, M.; Alshehri, S.M. International Journal of Biological Macromolecules Ultra-fast spill oil recovery using a mesoporous lignin based nanocomposite prepared from date palm pits (Phoenix dactylifera L.). Int. J. Biol. Macromol. 2019, 130, 139-147.
128. Silva, C.P.; Jaria, G.; Otero, M.; Esteves, V.I.; Calisto, V. Waste-based alternative adsorbents for the remediation of pharmaceutical contaminated waters: Has a step forward already been taken? Bioresour. Technol. 2018, 250, 888-901.
129. Anastopoulos, I.; Bhatnagar, A.; Hameed, B.H.; Ok, Y.S.; Omirou, M. A review on waste-derived adsorbents from sugar industry for pollutant removal in water and wastewater. J. Mol. Liq. 2017, 240, 179-188.
130. Sayehi, M.; Tounsi, H.; Garbarino, G.; Riani, P.; Busca, G. Reutilization of silicon- and aluminum- containing wastes in the perspective of the preparation of SiO2-Al2O3 based porous materials for adsorbents and catalysts. Waste Manag. 2020, 103, 146-158.
131. Gupta, V.K.; Carrott, P.J.M.; Ribeiro Carrott, M.M.L. Suhas Low-Cost adsorbents: Growing approach to wastewater treatmenta review. Crit. Rev. Environ. Sci. Technol. 2009, 39, 783-842.
132. Safarik, I.; Lunackova, P.; Weyda, F.; Safarikova, M. Adsorption of water-soluble organic dyes on ferrofluid- modified sawdust. Holzforschung 2007, 61, 247-253.
133. Safarik, I.; Safarikova, M. Magnetic fluid modified peanut husks as an adsorbent for organic dyes removal. Phys. Procedia 2010, 9, 274-278.
134. Zuorro, A.; Di Battista, A.; Lavecchia, R. Magnetically modified coffee silverskin for the removal of xenobiotics from wastewater. Chem. Eng. Trans. 2013, 35, 1375-1380.
135. Minh, T.P.; Lebedeva, O.E. Adsorption Properties of a Magnetite Composite with Coffee Waste. Russ. J. Phys. Chem. A 2018, 92, 2044-2047.
136. Stan, M.; Lung, I.; Soran, M.; Opris, O.; Leostean, C.; Popa, A.; Copaciu, F.; Diana, M.; Kacso, I.; Silipas, T.; et al. Starch-coated green synthesized magnetite nanoparticles for removal of textile dye Optilan Blue from aqueous media. J. Taiwan Inst. Chem. Eng. 2019, 100, 65-73.
137. Aydin, S. Removal of Organophosphorus Pesticides from Aqueous Solution by Magnetic Fe3O4/Red Mud- Nanoparticles. Water Environ. Res. 2016, 88, 2275-2284.
138. Aydin, S.; Aydin, M.E.; Beduk, F.; Ulvi, A. Removal of antibiotics from aqueous solution by using magnetic Fe3O4/red mud-nanoparticles. Sci. Total Environ. 2019, 670, 539-546.
139. Madrakian, T.; Afkhami, A.; Ahmadi, M. Adsorption and kinetic studies of seven different organic dyes onto magnetite nanoparticles loaded tea waste and removal of them from wastewater samples. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 2012, 99, 102-109.
140. Madrakian, E.; Ghaemi, E.; Ahmadi, M. Magnetic Solid Phase Extraction and Removal of Five Cationic Dyes from Aqueous Solution Using Magnetite Nanoparticle Loaded Platanusorientalis Waste Leaves. Anal. Bioanal. Chem. Res. 2016, 3, 279-286.
141. Sun, L.; Yuan, D.; Wan, S.; Yu, Z.; Dang, J. Adsorption Performance and Mechanisms of Methylene Blue Removal by Non-magnetic and Magnetic Particles Derived from the Vallisneria natans Waste. J. Polym. Environ. 2018, 26, 2992-3004.
142. Yu, J.X.; Wang, L.Y.; Chi, R.A.; Zhang, Y.F.; Xu, Z.G.; Guo, J. A simple method to prepare magnetic modified beer yeast and its application for cationic dye adsorption. Environ. Sci. Pollut. Res. 2013, 20, 543-551.
143. Magnacca, G.; Allera, A.; Montoneri, E.; Celi, L.; Benito, D.E.; Gagliardi, L.G.; Carlos, L. Novel magnetite nanoparticles coated with waste sourced bio- based substances as sustainable and renewable adsorbing materials. ACS Sustain. Chem. Eng. 2014, 2, 1518-1524.
144. Nisticò, R.; Cesano, F.; Franzoso, F.; Magnacca, G.; Scarano, D.; Funes, I.G.; Carlos, L.; Parolo, M.E. From biowaste to magnet-responsive materials for water remediation from polycyclic aromatic hydrocarbons. Chemosphere 2018, 202, 686-693.
145. Nisticò, R.; Celi, L.R.; Bianco Prevot, A.; Carlos, L.; Magnacca, G.; Zanzo, E.; Martin, M. Sustainable magnet-responsive nanomaterials for the removal of arsenic from contaminated water. J. Hazard. Mater. 2018, 342, 260-269.
146. Liu, J.; Yu, Y.; Zhu, S.; Yang, J.; Song, J.; Fan, W.; Yu, H.; Bian, D.; Huo, M. Synthesis and characterization of a magnetic adsorbent from negatively-valued iron mud for methylene blue adsorption. PLoS ONE 2018, 13, e0191229.
Marcos E. Peralta1, Santiago Ocampo1, Israel G. Funes2, Florencia Onaga Medina2, María E. Parolo2 and Luciano Carlos1,*
1Instituto de Investigación y Desarrollo en Ingeniería de Procesos, Biotecnología y Energías Alternativas, PROBIEN (CONICET-UNCo), Buenos Aires 1400, Neuquén 8300, Argentina
2Centro de Investigación en Toxicología Ambiental y Agrobiotecnología, CITAAC (CONICET-UNCo), Facultad de Ingeniería, Universidad Nacional del Comahue, Buenos Aires 1400, Neuquén 8300, Argentina
*Author to whom correspondence should be addressed.
© 2020. This work is licensed under http://creativecommons.org/licenses/by/3.0/ (the “License”). Notwithstanding the ProQuest Terms and Conditions, you may use this content in accordance with the terms of the License.